Abrasive particles and methods of making and using the same

ABSTRACT

Abrasive particles comprising ceramic (including glasses, crystalline ceramics, and glass-ceramics) comprising (on a theoretical oxide basis) Al 2 O 3  and at least one other metal oxide (e.g., REO and; REO and at least one of ZrO 2  or HfO 2 ) and methods of making the same. The abrasive particles can be incorporated into a variety of abrasive articles, including bonded abrasives, coated abrasives, nonwoven abrasives, and abrasive brushes.

This application is a continuation-in-part of U.S. Ser. No. 09/922,528, filed Aug. 2, 2001 now abandoned, the disclosure of which is incorporated herein by reference.

FIELD OF THE INVENTION

This invention relates to abrasive particles and methods of making the same. The abrasive particles can be incorporated into a variety of abrasive articles, including bonded abrasives, coated abrasives, nonwoven abrasives, and abrasive brushes.

DESCRIPTION OF RELATED ART

A large number of amorphous (including glass) and glass-ceramic compositions are known. The majority of oxide glass systems utilize well-known glass-formers such as SiO₂, B₂O₃, P₂O₅, GeO₂, TeO₂, As₂O₃, and V₂O₅ to aid in the formation of the glass. Some of the glass compositions formed with these glass-formers can be heat-treated to form glass-ceramics. The upper use temperature of glasses and glass-ceramics formed from such glass formers is generally less than 1200° C., typically about 700–800° C. The glass-ceramics tend to be more temperature resistant than the glass from which they are formed.

In addition, many properties of known glasses and glass-ceramics are limited by the intrinsic properties of glass-formers. For example, for SiO₂, B₂O₃, and P₂O₅-based glasses and glass-ceramics, the Young's modulus, hardness, and strength are limited by such glass-formers. Such glass and glass-ceramics generally have inferior mechanical properties as compared, for example, to Al₂O₃ or ZrO₂. Glass-ceramics having any mechanical properties similar to that of Al₂O₃ or ZrO₂ would be desirable.

Although some non-conventional glasses such as glasses based on rare earth oxide-aluminum oxide (see, e.g., PCT application having publication No. WO 01/27046 A1, published Apr. 19, 2001, and Japanese Document No. JP 2000-045129, published Feb. 15, 2000) are known, additional novel glasses and glass-ceramic, as well as use for both known and novel glasses and glass-ceramics is desired.

In another aspect, a variety of abrasive particles (e.g., diamond particles, cubic boron nitride particles, fused abrasive particles, and sintered, ceramic abrasive particles (including sol-gel-derived abrasive particles) known in the art. In some abrading applications, the abrasive particles are used in loose form, while in others the particles are incorporated into abrasive products (e.g., coated abrasive products, bonded abrasive products, non-woven abrasive products, and abrasive brushes). Criteria used in selecting abrasive particles used for a particular abrading application include: abrading life, rate of cut, substrate surface finish, grinding efficiency, and product cost.

From about 1900 to about the mid-1980's, the premier abrasive particles for abrading applications such as those utilizing coated and bonded abrasive products were typically fused abrasive particles. There are two general types of fused abrasive particles: (1) fused alpha alumina abrasive particles (see, e.g., U.S. Pat. Nos. 1,161,620 (Coulter), 1,192,709 (Tone), 1,247,337 (Saunders et al.), 1,268,533 (Allen), and 2,424,645 (Baumann et al.)), and (2) fused (sometimes also referred to as “co-fused”) alumina-zirconia abrasive particles (see, e.g., U.S. Pat. Nos. 3,891,408 (Rowse et al.), 3,781,172 (Pen et al.), 3,893,826 (Quinan et al.), 4,126,429 (Watson), 4,457,767 (Poon et al.), and 5,143,522 (Gibson et al.)) (also see, e.g., U.S. Pat. Nos. 5,023,212 (Dubots et al.) and 5,336,280 (Dubots et al.) which report the certain fused oxynitride abrasive particles). Fused alumina abrasive particles are typically made by charging a furnace with an alumina source such as aluminum ore or bauxite, as well as other desired additives, heating the material above its melting point, cooling the melt to provide a solidified mass, crushing the solidified mass into particles, and then screening and grading the particles to provide the desired abrasive particle size distribution. Fused alumina-zirconia abrasive particles are typically made in a similar manner, except the furnace is charged with both an alumina source and a zirconia source, and the melt is more rapidly cooled than the melt used to make fused alumina abrasive particles. For fused alumina-zirconia abrasive particles, the amount of alumina source is typically about 50–80 percent by weight, and the amount of zirconia, 50–20 percent by weight zirconia. The processes for making the fused alumina and fused alumina abrasive particles may include removal of impurities from the melt prior to the cooling step.

Although fused alpha alumina abrasive particles and fused alumina-zirconia abrasive particles are still widely used in abrading applications (including those utilizing coated and bonded abrasive products, the premier abrasive particles for many abrading applications since about the mid-1980's are sol-gel-derived alpha alumina particles (see, e.g., U.S. Pat. Nos. 4,314,827 (Leitheiser et al.), 4,518,397 (Leitheiser et al.), 4,623,364 (Cottringer et al.), 4,744,802 (Schwabel), 4,770,671 (Monroe et al.), 4,881,951 (Wood et al.), 4,960,441 (Pellow et al.), 5,139,978 (Wood), 5,201,916 (Berg et al.), 5,366,523 (Rowenhorst et al.), 5,429,647 (Larmie), 5,547,479 (Conwell et al.), 5,498,269 (Larmie), 5,551,963 (Larmie), and 5,725,162 (Garg et al.)).

The sol-gel-derived alpha alumina abrasive particles may have a microstructure made up of very fine alpha alumina crystallites, with or without the presence of secondary phases added. The grinding performance of the sol-gel-derive abrasive particles on metal, as measured, for example, by life of abrasive products made with the abrasive particles was dramatically longer than such products made from conventional fused alumina abrasive particles.

Typically, the processes for making sol-gel-derived abrasive particles are more complicated and expensive than the processes for making conventional fused abrasive particles. In general, sol-gel-derived abrasive particles are typically made by preparing a dispersion or sol comprising water, alumina monohydrate (boehmite), and optionally peptizing agent (e.g., an acid such as nitric acid), gelling the dispersion, drying the gelled dispersion, crushing the dried dispersion into particles, screening the particles to provide the desired sized particles, calcining the particles to remove volatiles, sintering the calcined particles at a temperature below the melting point of alumina, and screening and grading the particles to provide the desired abrasive particle size distribution. Frequently a metal oxide modifier(s) is incorporated into the sintered abrasive particles to alter or otherwise modify the physical properties and/or microstructure of the sintered abrasive particles.

There are a variety of abrasive products (also referred to “abrasive articles”) known in the art. Typically, abrasive products include binder and abrasive particles secured within the abrasive product by the binder. Examples of abrasive products include: coated abrasive products, bonded abrasive products, nonwoven abrasive products, and abrasive brushes.

Examples of bonded abrasive products include: grinding wheels, cutoff wheels, and honing stones. The main types of bonding systems used to make bonded abrasive products are: resinoid, vitrified, and metal. Resinoid bonded abrasives utilize an organic binder system (e.g., phenolic binder systems) to bond the abrasive particles together to form the shaped mass (see, e.g., U.S. Pat. Nos. 4,741,743 (Narayanan et al.), 4,800,685 (Haynes et al.), 5,037,453 (Narayanan et al.), and 5,110,332 (Narayanan et al.)). Another major type are vitrified wheels in which a glass binder system is used to bond the abrasive particles together mass (see, e.g., U.S. Pat. Nos. 4,543,107 (Rue), 4,898,587 (Hay et al.), 4,997,461 (Markhoff-Matheny et al.), and 5,863,308 (Qi et al.)). These glass bonds are usually matured at temperatures between 900° C. to 1300° C. Today vitrified wheels utilize both fused alumina and sol-gel-derived abrasive particles. However, fused alumina-zirconia is generally not incorporated into vitrified wheels due in part to the thermal stability of alumina-zirconia. At the elevated temperatures at which the glass bonds are matured, the physical properties of alumina-zirconia degrade, leading to a significant decrease in their abrading performance. Metal bonded abrasive products typically utilize sintered or plated metal to bond the abrasive particles.

The abrasive industry continues to desire abrasive particles and abrasive products that are easier to make, cheaper to make, and/or provide performance advantage(s) over conventional abrasive particles and products.

SUMMARY OF THE INVENTION

The present invention provides abrasive particles comprising ceramic (including amorphous materials, glasses, crystalline ceramics (e.g., crystallites of a complex metal oxide(s) (e.g., complex Al₂O₃.REO)), and glass-ceramics) comprising (on a theoretical oxide basis; e.g., may be present as a reaction product (e.g., CeAl₁₁O₁₈)), Al₂O₃ and at least one other metal oxide (e.g., REO and; REO and at least one of ZrO₂ or HfO₂). In one aspect, abrasive particles according to the present invention typically have an average hardness (i.e., resistance to deformation; also referred to as (“microhardness”); determined as described in the “Detailed Description (below) of at least, 15 GPa, 16 GPa, 17 GPa, or even at least 18 GPa (or more). In one aspect, the ceramic comprising the abrasive particles according to the present invention may comprise, for example, less than 40 (35, 30, 25, 20, 15, 10, 5, 3, 2, 1, or even zero) percent by weight traditional glass formers such as SiO₂, B₂O₃, P₂O₅, GeO₂, TeO₂, and/or combinations thereof, based on the total weight of the ceramic. In another aspect, the ceramic comprising the abrasive particles according to the present invention typically comprise, for example, zero, less than 25, 20, 15, 10, 5, 4, 3, 2, or 1 percent by volume amorphous material. In another aspect, the ceramic comprising the abrasive particles according to the present invention typically comprise, for example, at least 75, 80, 85, 90, 95, 97, 98, 99, or even 100 percent by volume crystalline ceramic.

Some embodiments desirably, the ceramic comprising the abrasive particles according to the present invention comprise at least 30 (more desirably, in a range of about 30 to about 60) percent by weight of the Al₂O₃, based on the total weight of the ceramic. In another aspect, some embodiments desirably, the ceramic comprising the abrasive particles according to the present invention comprise crystalline ceramic, wherein some embodiments include those wherein the ceramic (a) exhibits a microstructure comprising crystallites (e.g., crystallites of a complex metal oxide(s) (e.g., complex Al₂O₃.REO)) having an average crystallite size of less than 1 micrometer (typically, less than 500 nanometers, even less than 300 or 150 nanometers; and in some embodiments, less than 20 nanometers), and (b) is free of at least one of eutectic microstructure features (i.e., is free of colonies and lamellar structure) or a non-cellular microstructure. It is also within the scope of the present invention for some embodiments to have at least one crystalline phase within a specified average crystallite value and at least one (different) crystalline phase outside of a specified average crystallite value.

Some embodiments of abrasive particles according to the present invention comprise glass-ceramic comprising Al₂O₃ and at least one other metal oxide (e.g., REO and; REO and at least one of ZrO₂ or HfO₂;), wherein at least 80 (85, 90, 95, 97, 98, 99, or even 100) percent by weight of the glass-ceramic collectively comprises the Al₂O₃ and at least one other metal oxide, based on the total weight of the glass-ceramic. The glass-ceramic may comprise, for example, at least 1, 2, 3, 5, 10, 15, 20, 25, 30, 35, 40, 45, 50, 55, 60, 65, 70, 75, 80, 85, 90, or 95 percent by volume amorphous material. The glass-ceramic may comprise, for example, at least 99, 98, 97, 95, 90, 85, 80, 75, 70, 65, 60, 55, 50, 45, 40, 35, 30, 25, 20, 15, 10, or 5 percent by volume crystalline ceramic.

Some embodiments of abrasive particles according to the present invention comprise glass-ceramic comprising Al₂O₃ and at least one other metal oxide (e.g., REO and; REO and at least one of ZrO₂ or HfO₂), wherein at least 60 (65, 70, 75, 80, 85, 90, 95, 97, 98, 99, or even 100) percent by weight of the glass-ceramic collectively comprises the Al₂O₃ and at least one other metal oxide, and less than 20 (preferably, less than 15, 10, 5, or even 0) percent by weight SiO₂, and less than 20 (preferably, less than 15, 10, 5, or even 0) percent by weight B₂O₃, based on the total weight of the glass-ceramic. The glass-ceramic may comprise, for example, at least 1, 2, 3, 5, 10, 15, 20, 25, 30, 35, 40, 45, 50, 55, 60, 65, 70, 75, 80, 85, 90, or 95 percent by volume amorphous material. The glass-ceramic may comprise, for example, at least 99, 98, 97, 95, 90, 85, 80, 75, 70, 65, 60, 55, 50, 45, 40, 35, 30, 25, 20, 15, 10, or 5 percent by volume crystalline ceramic.

Some embodiments of abrasive particles according to the present invention comprise glass-ceramic comprising Al₂O₃ and at least one other metal oxide (e.g., REO and; REO and at least one of ZrO₂ or HfO₂), wherein at least 60 (65, 70, 75, 80, 85, 90, 95, 97, 98, 99, or even 100) percent by weight of the glass-ceramic collectively comprises the Al₂O₃ and at least one other metal oxide, and less than 40 percent (preferably, less than 35, 30, 25, 20, 15, 10, 5, or even 0) by weight collectively SiO₂, B₂O₃, and P₂O₅, based on the total weight of the glass-ceramic. The glass-ceramic may comprise, for example, at least 1, 2, 3, 5, 10, 15, 20, 25, 30, 35, 40, 45, 50, 55, 60, 65, 70, 75, 80, 85, 90, 95, percent by volume amorphous material. The glass-ceramic may comprise, for example, at least 99, 98, 97, 95, 90, 85, 80, 75, 70, 65, 60, 55, 50, 45, 40, 35, 30, 25, 20, 15, 10, or 5 percent by volume crystalline ceramic.

Some embodiments of abrasive particles according to the present invention comprise glass-ceramic comprising Al₂O₃ and at least one other metal oxide (e.g., REO and; REO and at least one of ZrO₂ or HfO₂), wherein the glass-ceramic (a) exhibits a microstructure comprising crystallites (e.g., crystallites of a complex metal oxide(s) (e.g., complex Al₂O₃.REO)) having an average crystallite size of less than 1 micrometer (typically, less than 500 nanometers, or even less than 300 or 150 nanometers; and in some embodiments, less than 20 nanometers), and (b) is free of eutectic microstructure features. Some embodiments of abrasive particles according to the present invention comprise glass-ceramic comprising Al₂O₃ and at least one other metal oxide (e.g., REO and; REO and at least one of ZrO₂ or HfO₂), wherein the glass-ceramic (a) exhibits a non-cellular microstructure comprising crystallites (e.g., crystallites of a complex metal oxide(s) (e.g., complex Al₂O₃.REO)) having an average crystallite size of less than 1 micrometer (typically, less than 500 nanometers, even less than 300 or 150 nanometers; and in some embodiments, less than 20 nanometers). The glass-ceramic may comprise, for example, at least 1, 2, 3, 5, 10, 15, 20, 25, 30, 35, 40, 45, 50, 55, 60, 65, 70, 75, 80, 85, 90, 95, percent by volume amorphous material. The glass-ceramic may comprise, for example, at least 99, 98, 97, 95, 90, 85, 80, 75, 70, 65, 60, 55, 50, 45, 40, 35, 30, 25, 20, 15, 10, or 5 percent by volume crystalline ceramic. It is also within the scope of the present invention for some embodiments to have at least one crystalline phase within a specified average crystallite value and at least one (different) crystalline phase outside of a specified average crystallite value.

Some embodiments of abrasive particles according to the present invention comprise ceramic comprising crystalline ceramic (e.g., at least 1, 2, 3, 5, 10, 15, 20, 25, 30, 35, 40, 45, 50, 55, 60, 65, 70, 75, 80, 85, 90, 95, 97, 98, 99, or even 100 percent by volume crystalline ceramic), the crystalline ceramic comprising Al₂O₃ and at least one other metal oxide (e.g., REO and; REO and at least one of ZrO₂ or HfO₂), wherein at least 80 (85, 90, 95, 97, 98, 99, or even 100) percent by weight of the crystalline ceramic collectively comprises the Al₂O₃ and at least one other metal oxide, based on the total weight of the crystalline ceramic. Some desirable embodiments include those wherein the ceramic (a) exhibits a microstructure comprising crystallites (e.g., crystallites of a complex metal oxide(s) (e.g., complex Al₂O₃.REO)) having an average crystallite size of less than 1 micrometer (typically, less than 500 nanometers, or even less than 300 or 150 nanometers; and in some embodiments, less than 20 nanometers), and (b) is free of eutectic microstructure features. Some embodiments of abrasive particles according to the present invention include those wherein the ceramic (a) exhibits a non-cellular microstructure comprising crystallites (e.g., crystallites of a complex metal oxide(s) (e.g., complex Al₂O₃.REO)) having an average crystallite size of less than 1 micrometer (typically, less than 500 nanometers, even less than 300 or 150 nanometers; and in some embodiments, less than 20 nanometers). The ceramic may comprise, for example, at least 99, 98, 97, 95, 90, 85, 80, 75, 70, 65, 60, 55, 50, 45, 40, 35, 30, 25, 20, 15, 10, 5, 3, 2, or 1 percent by volume amorphous material. It is also within the scope of the present invention for some embodiments to have at least one crystalline phase within a specified average crystallite value and at least one (different) crystalline phase outside of a specified average crystallite value.

Some embodiments of abrasive particles according to the present invention comprise ceramic comprising crystalline ceramic (e.g., at least 1, 2, 3, 5, 10, 15, 20, 25, 30, 35, 40, 45, 50, 55, 60, 65, 70, 75, 80, 85, 90, 95, 97, 98, 99, or even 100 percent by volume crystalline ceramic), the crystalline ceramic comprising Al₂O₃ and at least one other metal oxide (e.g., REO and; REO and at least one of ZrO₂ or HfO₂), wherein at least 60 (65, 70, 75, 80, 85, 90, 95, 97, 98, 99, or even 100) percent by weight of the crystalline ceramic collectively comprises the Al₂O₃ and at least one other metal oxide, and less than 20 (preferably, less than 15, 10, 5, or even 0) percent by weight SiO₂, and less than 20 (preferably, less than 15, 10, 5, or even 0) percent by weight B₂O₃, based on the total weight of the crystalline ceramic. Some desirable embodiments include those wherein the ceramic (a) exhibits a microstructure comprising crystallites (e.g., crystallites of a complex metal oxide(s) (e.g., complex Al₂O₃.REO)) having an average crystallite size of less than 1 micrometer (typically, less than 500 nanometers, or even less than 300 or 150 nanometers; and in some embodiments, less than 20 nanometers), and (b) is free of eutectic microstructure features. Some embodiments of abrasive particles according to the present invention include those wherein the ceramic (a) exhibits a non-cellular microstructure comprising crystallites (e.g., crystallites of a complex metal oxide(s) (e.g., complex Al₂O₃.REO)) having an average crystallite size of less than 1 micrometer (typically, less than 500 nanometers, even less than 300 or 150 nanometers; and in some embodiments, less than 20 nanometers). The ceramic may comprise, for example, at least 99, 98, 97, 95, 90, 85, 80, 75, 70, 65, 60, 55, 50, 45, 40, 35, 30, 25, 20, 15, 10, 5, 3, 2, or 1 percent by volume amorphous material. It is also within the scope of the present invention for some embodiments to have at least one crystalline phase within a specified average crystallite value and at least one (different) crystalline phase outside of a specified average crystallite value.

Some embodiments of abrasive particles according to the present invention comprise ceramic comprising crystalline ceramic (e.g., at least 1, 2, 3, 5, 10, 15, 20, 25, 30, 35, 40, 45, 50, 55, 60, 65, 70, 75, 80, 85, 90, 95, 97, 98, 99, or even 100 percent by volume crystalline ceramic), the crystalline ceramic comprising Al₂O₃ and at least one other metal oxide (e.g., REO and; REO and at least one of ZrO₂ or HfO₂), wherein at least 60 (65, 70, 75, 80, 85, 90, 95, 97, 98, 99, or even 100) percent by weight of the crystalline ceramic collectively comprises the Al₂O₃ and at least one other metal oxide, and less than 40 (preferably, less than 35, 30, 25, 20, 15, 10, 5, or even 0) percent by weight collectively SiO₂, B₂O₃, and P₂O₅, based on the total weight of the crystalline ceramic. Some desirable embodiments include those wherein the ceramic (a) exhibits a microstructure comprising crystallites (e.g., crystallites of a complex metal oxide(s) (e.g., complex Al₂O₃.REO)) having an average crystallite size of less than 1 micrometer (typically, less than 500 nanometers, or even less than less than 300 or 150 nanometers; and in some embodiments, less than 20 nanometers), and (b) is free of eutectic microstructure features. Some embodiments of abrasive particles according to the present invention include those wherein the ceramic (a) exhibits a non-cellular microstructure comprising crystallites (e.g., crystallites of a complex metal oxide(s) (e.g., complex Al₂O₃.REO)) having an average crystallite size of less than 1 micrometer (typically, less than 500 nanometers, even less than 300 or 150 nanometers; and in some embodiments, less than 20 nanometers). The ceramic may comprise, for example, at least 99, 98, 97, 95, 90, 85, 80, 75, 70, 65, 60, 55, 50, 45, 40, 35, 30, 25, 20, 15, 10, 5, 3, 2, or 1 percent by volume amorphous material. It is also within the scope of the present invention for some embodiments to have at least one crystalline phase within a specified average crystallite value and at least one (different) crystalline phase outside of a specified average crystallite value.

Some embodiments of abrasive particles according to the present invention comprise ceramic comprising crystalline ceramic (e.g., at least 1, 2, 3, 5, 10, 15, 20, 25, 30, 35, 40, 45, 50, 55, 60, 65, 70, 75, 80, 85, 90, 95, 97, 98, 99, or even 100 percent by volume crystalline ceramic), the ceramic comprising Al₂O₃ and at least one other metal oxide (e.g., REO and; REO and at least one of ZrO₂ or HfO₂). Desirable some embodiments include those wherein the ceramic (a) exhibits a microstructure comprising crystallites (e.g., crystallites of a complex metal oxide(s) (e.g., complex Al₂O₃.REO)) having an average crystallite size of less than 1 micrometer (typically, less than 500 nanometers, or even less than 300 or 150 nanometers; and in some embodiments, less than 20 nanometers), and (b) is free of eutectic microstructure features. Some embodiments of abrasive particles according to the present invention include those wherein the ceramic (a) exhibits a non-cellular microstructure comprising crystallites (e.g., crystallites of a complex metal oxide(s) (e.g., complex Al₂O₃.REO)) having an average crystallite size of less than 1 micrometer (typically, less than 500 nanometers, even less than 300 or 150 nanometers; and in some embodiments, less than 20 nanometers). The ceramic may comprise, for example, at least 99, 98, 97, 95, 90, 85, 80, 75, 70, 65, 60, 55, 50, 45, 40, 35, 30, 25, 20, 15, 10, 5, 3, 2, or 1 percent by volume amorphous material. It is also within the scope of the present invention for some embodiments to have at least one crystalline phase within a specified average crystallite value and at least one (different) crystalline phase outside of a specified average crystallite value.

Some embodiments of abrasive particles according to the present invention may comprise ceramic comprising crystalline ceramic (e.g., at least 1, 2, 3, 5, 10, 15, 20, 25, 30, 35, 40, 45, 50, 55, 60, 65, 70, 75, 80, 85, 90, 95, 97, 98, 99, or even 100 percent by volume crystalline ceramic), the ceramic comprising Al₂O₃ and at least one other metal oxide (e.g., REO and; REO and at least one of ZrO₂ or HfO₂), wherein at least 80 (85, 90, 95, 97, 98, 99, or even 100) percent by weight of the ceramic collectively comprises the Al₂O₃ and at least one other metal oxide, based on the total weight of the ceramic. Some desirable embodiments include those wherein the ceramic (a) exhibits a microstructure comprising crystallites (e.g., crystallites of a complex metal oxide(s) (e.g., complex Al₂O₃.REO)) having an average crystallite size of less than 1 micrometer (typically, less than 500 nanometers, or even less than 300 or 150 nanometers; and in some embodiments, less than 20 nanometers), and (b) is free of eutectic microstructure features. Some embodiments of abrasive particles according to the present invention include those wherein the ceramic (a) exhibits a non-cellular microstructure comprising crystallites (e.g., crystallites of a complex metal oxide(s) (e.g., complex Al₂O₃.REO)) having an average crystallite size of less than 1 micrometer (typically, less than 500 nanometers, even less than 300 or 150 nanometers; and in some embodiments, less than 20 nanometers). The ceramic may comprise, for example, at least 99, 98, 97, 95, 90, 85, 80, 75, 70, 65, 60, 55, 50, 45, 40, 35, 30, 25, 20, 15, 10, 5, 3, 2, or 1 percent by volume amorphous material. It is also within the scope of the present invention for some embodiments to have at least one crystalline phase within a specified average crystallite value and at least one (different) crystalline phase outside of a specified average crystallite value.

Some embodiments of abrasive particles according to the present invention may comprise ceramic comprising crystalline ceramic (e.g., at least 1, 2, 3, 5, 10, 15, 20, 25, 30, 35, 40, 45, 50, 55, 60, 65, 70, 75, 80, 85, 90, 95, 97, 98, 99, or even 100 percent by volume crystalline ceramic), the ceramic comprising Al₂O₃ and at least one other metal oxide (e.g., REO and; REO and at least one of ZrO₂ or HfO₂), wherein at least 60 (65, 70, 75, 80, 85, 90, 95, 97, 98, 99, or even 100) percent by weight of the ceramic collectively comprises the Al₂O₃ and at least one other metal oxide, and less than 20 (preferably, less than 15, 10, 5, or even 0) percent by weight SiO₂ and less than 20 (preferably, less than 15, 10, 5, or even 0) percent by weight B₂O₃, based on the total weight of the ceramic. Some desirable embodiments include those wherein the ceramic (a) exhibits a microstructure comprising crystallites (e.g., crystallites of a complex metal oxide(s) (e.g., complex Al₂O₃.REO)) having an average crystallite size of less than 1 micrometer (typically, less than 500 nanometers, or even less than 300 or 150 nanometers; and in some embodiments, less than 20 nanometers), and (b) is free of eutectic microstructure features. Some embodiments of abrasive particles according to the present invention include those wherein the ceramic (a) exhibits a non-cellular microstructure comprising crystallites (e.g., crystallites of a complex metal oxide(s) (e.g., complex Al₂O₃.REO)) having an average crystallite size of less than 1 micrometer (typically, less than 500 nanometers, even less than 300 or 150 nanometers; and in some embodiments, less than 20 nanometers). The ceramic may comprise, for example, at least 99, 98, 97, 95, 90, 85, 80, 75, 70, 65, 60, 55, 50, 45, 40, 35, 30, 25, 20, 15, 10, 5, 3, 2, or 1 percent by volume amorphous material. It is also within the scope of the present invention for some embodiments to have at least one crystalline phase within a specified average crystallite value and at least one (different) crystalline phase outside of a specified average crystallite value.

Some embodiments of abrasive particles according to the present invention may comprise ceramic comprising crystalline ceramic (e.g., at least 1, 2, 3, 5, 10, 15, 20, 25, 30, 35, 40, 45, 50, 55, 60, 65, 70, 75, 80, 85, 90, 95, 97, 98, 99, or even 100 percent by volume crystalline ceramic), the ceramic comprising Al₂O₃ and at least one other metal oxide (e.g., REO and; REO and at least one of ZrO₂ or HfO₂), wherein at least 60 (65, 70, 75, 80, 85, 90, 95, 97, 98, 99, or even 100) percent by weight of the ceramic collectively comprises the Al₂O₃ and at least one other metal oxide, and less than 40 (preferably, less than 35, 30, 25, 20, 15, 10, 5, or even 0) percent by weight collectively SiO₂, B₂O₃, and P₂O₅, based on the total weight of the ceramic. Desirable some embodiments include those wherein the ceramic (a) exhibits a microstructure comprising crystallites (e.g., crystallites of a complex metal oxide(s) (e.g., complex Al₂O₃.REO)) having an average crystallite size of less than 1 micrometer (typically, less than 500 nanometers, or even less than 300 or 150 nanometers; and in some embodiments, less than 20 nanometers), and (b) is free of eutectic microstructure features. Some embodiments of abrasive particles according to the present invention include those wherein the ceramic (a) exhibits a non-cellular microstructure comprising crystallites (e.g., crystallites of a complex metal oxide(s) (e.g., complex Al₂O₃.REO)) having an average crystallite size of less than 1 micrometer (typically, less than 500 nanometers, even less than 300 or 150 nanometers; and in some embodiments, less than 20 nanometers). The ceramic may comprise, for example, at least 99, 98, 97, 95, 90, 85, 80, 75, 70, 65, 60, 55, 50, 45, 40, 35, 30, 25, 20, 15, 10, 5, 3, 2, or 1 percent by volume amorphous material. It is also within the scope of the present invention for some embodiments to have at least one crystalline phase within a specified average crystallite value and at least one (different) crystalline phase outside of a specified average crystallite value.

Some embodiments of abrasive particles according to the present invention may comprise glass-ceramic comprising Al₂O₃ and REO, wherein the glass-ceramic (a) exhibits a microstructure comprising crystallites (e.g., crystallites of a complex metal oxide(s) (e.g., complex Al₂O₃.REO)) having an average crystallite size of less than 200 nanometers (150 nanometers, 100 nanometers, 75 nanometers, or even 50 nanometers) and (b) has a density of at least 90% (95%, 96%, 97%, 98%, 99%, 99.5%, or 100%) of theoretical density. Some embodiments can be free of at least one of eutectic microstructure features or a non-cellular microstructure. It is also within the scope of the present invention for some embodiments to have at least one crystalline phase within a specified average crystallite value and at least one (different) crystalline phase outside of a specified average crystallite value.

Some embodiments of abrasive particles according to the present invention may comprise glass-ceramic comprising Al₂O₃ and REO, wherein the glass-ceramic (a) exhibits a microstructure comprising crystallites (e.g., crystallites of a complex metal oxide(s) (e.g., complex Al₂O₃.REO)), wherein none of the crystallites are greater than 200 nanometers (150 nanometers, 100 nanometers, 75 nanometers, or even 50 nanometers) in size and (b) has a density of at least 90% (95%, 96%, 97%, 98%, 99%, 99.5%, or 100%) of theoretical density. Some embodiments can be free of at least one of eutectic microstructure features or a non-cellular microstructure. It is also within the scope of the present invention for some embodiments to have at least one crystalline phase within a specified crystallite value and at least one (different) crystalline phase outside of a specified crystallite value.

Some embodiments of abrasive particles according to the present invention may comprise glass-ceramic comprising Al₂O₃ and REO, wherein the glass-ceramic (a) exhibits a microstructure comprising crystallites (e.g., crystallites of a complex metal oxide(s) (e.g., complex Al₂O₃.REO)), wherein at least a portion of the crystallites are not greater than 150 nanometers (100 nanometers, 75 nanometers, or even 50 nanometers) in size and (b) has a density of at least 90% (95%, 96%, 97%, 98%, 99%, 99.5%, or 100%) of theoretical density. Some embodiments can be free of at least one of eutectic microstructure features or a non-cellular microstructure. It is also within the scope of the present invention for some embodiments to have at least one crystalline phase within a specified crystallite value and at least one (different) crystalline phase outside of a specified crystallite value.

Some embodiments of abrasive particles according to the present invention may comprise fully crystallized glass-ceramic comprising Al₂O₃ and REO, wherein the glass-ceramic (a) exhibits a microstructure comprising crystallites (e.g., crystallites of a complex metal oxide(s) (e.g., complex Al₂O₃.REO)) having an average crystallite size not greater than 1 micrometer (500 nanometers, 300 nanometers, 200 nanometers, 150 nanometers, 100 nanometers, 75 nanometers, or even 50 nanometers) in size and (b) has a density of at least 90% (95%, 96%, 97%, 98%, 99%, 99.5%, or 100%) of theoretical density. Some embodiments can be free of at least one of eutectic microstructure features or a non-cellular microstructure. It is also within the scope of the present invention for some embodiments to have at least one crystalline phase within a specified crystallite value and at least one (different) crystalline phase outside of a specified crystallite value.

Some embodiments of abrasive particles according to the present invention may comprise ceramic comprising crystalline ceramic, wherein the ceramic comprises Al₂O₃ and REO, and (a) exhibits a microstructure comprising crystallites (e.g., crystallites of a complex metal oxide(s) (e.g., complex Al₂O₃.REO)) having an average crystallite size of less than 200 nanometers (150 nanometers, 100 nanometers, or even 50 nanometers) and (b) has a density of at least 90% (95%, 96%, 97%, 98%, 99%, 99.5%, or 100%) of theoretical density. Some embodiments can be free of at least one of eutectic microstructure features or a non-cellular microstructure. It is also within the scope of the present invention for some embodiments to have at least one crystalline phase within a specified average crystallite value and at least one (different) crystalline phase outside of a specified average crystallite value.

Some embodiments of abrasive particles according to the present invention may comprise ceramic comprising crystalline ceramic, wherein the ceramic comprises Al₂O₃ and REO, and (a) exhibits a microstructure comprising crystallites (e.g., crystallites of a complex metal oxide(s) (e.g., complex Al₂O₃.REO)), wherein none of the crystallites are greater than 200 nanometers (150 nanometers, 100 nanometers, 75 nanometers, or even 50 nanometers) in size and (b) has a density of at least 90% (95%, 96%, 97%, 98%, 99%, 99.5%, or 100%) of theoretical density. Some embodiments can be free of at least one of eutectic microstructure features or a non-cellular microstructure. It is also within the scope of the present invention for some embodiments to have at least one crystalline phase within a specified crystallite value and at least one (different) crystalline phase outside of a specified crystallite value.

Some embodiments of abrasive particles according to the present invention may comprise ceramic comprising crystalline ceramic, wherein the ceramic comprises Al₂O₃ and REO, and (a) exhibits a microstructure comprising crystallites (e.g., crystallites of a complex metal oxide(s) (e.g., complex Al₂O₃.REO)), wherein at least a portion of the crystallites are not greater than 150 nanometers (100 nanometers, 75 nanometers, or even 50 nanometers) in size and (b) has a density of at least 90% (95%, 96%, 97%, 98%, 99%, 99.5%, or 100%) of theoretical density. Some embodiments can be free of at least one of eutectic microstructure features or a non-cellular microstructure. It is also within the scope of the present invention for some embodiments to have at least one crystalline phase within a specified crystallite value and at least one (different) crystalline phase outside of a specified crystallite value.

Some embodiments of abrasive particles according to the present invention may comprise ceramic comprising crystalline ceramic, wherein the ceramic comprises Al₂O₃ and REO, and (a) exhibits a microstructure comprising crystallites (e.g., crystallites of a complex metal oxide(s) (e.g., complex Al₂O₃.REO)) having an average crystallite size not greater than 1 micrometer (500 nanometers, 300 nanometers, 200 nanometers, 150 nanometers, 100 nanometers, 75 nanometers, or even 50 nanometers) in size and (b) has a density of at least 90% (95%, 96%, 97%, 98%, 99%, 99.5%, or 100%) of theoretical density. Some embodiments can be free of at least one of eutectic microstructure features or a non-cellular microstructure. It is also within the scope of the present invention for some embodiments to have at least one crystalline phase within a specified crystallite value and at least one (different) crystalline phase outside of a specified crystallite value.

In this application:

“amorphous material” refers to material derived from a melt and/or a vapor phase that lacks any long range crystal structure as determined by X-ray diffraction and/or has an exothermic peak corresponding to the crystallization of the amorphous material as determined by a DTA (differential thermal analysis) as determined by the test described herein entitled “Differential Thermal Analysis”;

“ceramic” includes amorphous material, glass, crystalline ceramic, glass-ceramic, and combinations thereof;

“complex metal oxide” refers to a metal oxide comprising two or more different metal elements and oxygen (e.g., CeAl₁₁O₁₈, Dy₃Al₅O₁₂, MgAl₂O₄, and Y₃Al₅O₁₂);

“complex Al₂O₃.metal oxide” refers to a complex metal oxide comprising, on a theoretical oxide basis, Al₂O₃ and one or more metal elements other than Al (e.g., CeAl₁₁O₁₈, Dy₃Al₅O₁₂, MgAl₂O₄, and Y₃Al₅O₁₂);

“complex Al₂O₃.Y₂O₃” refers to a complex metal oxide comprising, on a theoretical oxide basis, Al₂O₃ and Y₂O₃ (e.g., Y₃Al₅O₁₂);

“complex Al₂O₃.REO” refers to a complex metal oxide comprising, on a theoretical oxide basis, Al₂O₃ and rare earth oxide (e.g., CeAl₁₁O₁₈ and Dy₃Al₅O₁₂);

“glass” refers to amorphous material exhibiting a glass transition temperature;

“glass-ceramic” refers to ceramics comprising crystals formed by heat-treating amorphous material;

“T_(g)” refers to the glass transition temperature as determined by the test described herein entitled “Differential Thermal Analysis”;

“T_(x)” refers to the crystallization temperature as determined by the test described herein entitled “Differential Thermal Analysis”;

“rare earth oxides” refers to cerium oxide (e.g., CeO₂), dysprosium oxide (e.g., Dy₂O₃), erbium oxide (e.g., Er₂O₃), europium oxide (e.g., Eu₂O₃), gadolinium (e.g., Gd₂O₃), holmium oxide (e.g., Ho₂O₃), lanthanum oxide (e.g., La₂O₃), lutetium oxide (e.g., Lu₂O₃), neodymium oxide (e.g., Nd₂O₃), praseodymium oxide (e.g., Pr₆O₁₁), samarium oxide (e.g., Sm₂O₃), terbium (e.g., Tb₂O₃), thorium oxide (e.g., Th₄O₇), thulium (e.g., Tm₂O₃), and ytterbium oxide (e.g., Yb₂O₃), and combinations thereof;

“REO” refers to rare earth oxide(s).

Further, it is understood herein that unless it is stated that a metal oxide (e.g., Al₂O₃, complex Al₂O₃.metal oxide, etc.) is crystalline, for example, in a glass-ceramic, it may be amorphous, crystalline, or portions amorphous and portions crystalline. For example if a glass-ceramic comprises Al₂O₃ and ZrO₂, the Al₂O₃ and ZrO₂ may each be in an amorphous state, crystalline state, or portions in an amorphous state and portions in a crystalline state, or even as a reaction product with another metal oxide(s) (e.g., unless it is stated that, for example, Al₂O₃ is present as crystalline Al₂O₃ or a specific crystalline phase of Al₂O₃ (e.g., alpha Al₂O₃), it may be present as crystalline Al₂O₃ and/or as part of one or more crystalline complex Al₂O₃.metal oxides.

Further, it is understood that glass-ceramics formed by heating amorphous material not exhibiting a T_(g) may not actually comprise glass, but rather may comprise the crystals and amorphous material that does not exhibiting a T_(g).

Abrasive articles according to the present invention comprise binder and a plurality of abrasive particles, wherein at least a portion of the abrasive particles are the abrasive particles according to the present invention. Exemplary abrasive products include coated abrasive articles, bonded abrasive articles (e.g., wheels), non-woven abrasive articles, and abrasive brushes. Coated abrasive articles typically comprise a backing having first and second, opposed major surfaces, and wherein the binder and the plurality of abrasive particles form an abrasive layer on at least a portion of the first major surface.

In some embodiments, preferably, at least 5, 10, 15, 20, 25, 30, 35, 40, 45, 50, 55, 60, 65, 70, 75, 80, 85, 90, 95, or even 100 percent by weight of the abrasive particles in an abrasive article are the abrasive particles according to the present invention, based on the total weight of the abrasive particles in the abrasive article.

Abrasive particles are usually graded to a given particle size distribution before use. Such distributions typically have a range of particle sizes, from coarse particles fine particles. In the abrasive art this range is sometimes referred to as a “coarse”, “control” and “fine” fractions. Abrasive particles graded according to industry accepted grading standards specify the particle size distribution for each nominal grade within numerical limits. Such industry accepted grading standards (i.e., specified nominal grades) include those known as the American National Standards Institute, Inc. (ANSI) standards, Federation of European Producers of Abrasive Products (FEPA) standards, and Japanese Industrial Standard (JIS) standards. In one aspect, the present invention provides a plurality of abrasive particles having a specified nominal grade, wherein at least a portion of the plurality of abrasive particles are abrasive particles according to the present invention. In some embodiments, preferably, at least 5, 10, 15, 20, 25, 30, 35, 40, 45, 50, 55, 60, 65, 70, 75, 80, 85, 90, 95, or even 100 percent by weight of the plurality of abrasive particles are the abrasive particles according to the present invention, based on the total weight of the plurality of abrasive particles.

Abrasive particles according to the present invention can be incorporated into various abrasive products such as coated abrasives, bonded abrasives, nonwoven abrasives, and abrasive brushes, as well as be used in loose form.

-   -   The present invention also provides a method of abrading a         surface, the method comprising:     -   contacting abrasive particles according to the present invention         with a surface of a workpiece; and     -   moving at least one of the abrasive particles according to the         present invention or the contacted surface to abrade at least a         portion of the surface with at least one of the abrasive         particles according to the present invention.

BRIEF DESCRIPTION OF THE DRAWING

FIG. 1 is a fragmentary cross-sectional schematic view of a coated abrasive article including abrasive particles according to the present invention;

FIG. 2 is a perspective view of a bonded abrasive article including abrasive particles according to the present invention;

FIG. 3 is an enlarged schematic view of a nonwoven abrasive article including abrasive particles according to the present invention;

FIG. 4 is a DTA curve of Example 1 material; and

FIGS. 5–8 is an SEM micrograph of Example 2, 6, 7, 8, 17, respectively, material heat-treated at 1300° C. for 1 hour.

DETAILED DESCRIPTION

Abrasive particles according to the present invention can be made by crystallizing amorphous material or ceramic comprising amorphous material to form glass-ceramic. In one aspect, amorphous materials for making abrasive particles according to the present invention include those comprising Al₂O₃, and at least one other metal oxide (e.g., REO and; REO and at least one of ZrO₂ or HfO₂), wherein at least 80 (85, 90, 95, 97, 98, 99, or even 100) percent by weight of the amorphous material collectively comprises the comprises the Al₂O₃, and at least one other metal oxide, based on the total weight of the amorphous material.

In another aspect, amorphous materials for making abrasive particles according to the present invention include those comprising Al₂O₃, and at least one other metal oxide (e.g., REO and; REO and at least one of ZrO₂ or HfO₂), wherein at least 60 (65, 70, 75, 80, 85, 90, 95, 97, 98, 99, or even 100) percent by weight of the amorphous material collectively comprises the Al₂O₃, and at least one other metal oxide, and less than 20 (preferably, less than 15, 10, 5, or even 0) percent by weight SiO₂ and less than 20 (preferably, less than 15, 10, 5, or even 0) percent by weight B₂O₃, based on the total weight of the amorphous material.

In another aspect, amorphous materials for making abrasive particles according to the present invention include those comprising Al₂O₃, and at least one other metal oxide (e.g., REO and; REO and at least one of ZrO₂ or HfO₂, wherein at least 60 (65, 70, 75, 80, 85, 90, 95, 97, 98, 99, or even 100) percent by weight of the amorphous material collectively comprises the Al₂O₃, and at least one other metal oxide, and less than 40 (preferably, less than 35, 30, 25, 20, 15, 10, 5, or even 0) percent by weight collectively SiO₂, B₂O₃, and P₂O₅, based on the total weight of the amorphous material.

Amorphous materials or ceramic comprising amorphous material can be made by heating (including in a flame) the appropriate metal oxide sources to form a melt, desirably a homogenous melt, and then rapidly cooling the melt to provide amorphous material. For example, amorphous materials can be made, for example, by heating (including in a flame) the appropriate metal oxide sources to form a melt, desirably a homogenous melt, and then rapidly cooling the melt to provide amorphous material. Some embodiments of amorphous materials can be made, for example, by melting the metal oxide sources in any suitable furnace (e.g., an inductive heated furnace, a gas-fired furnace, or an electrical furnace), or, for example, in a plasma. The resulting melt is cooled (e.g., discharging the melt into a cooling media (e.g., high velocity air jets, liquids, metal plates (including chilled metal plates), metal rolls (including chilled metal rolls), metal balls (including chilled metal balls), and the like)). In one method, amorphous materials and ceramic comprising amorphous materials can be made utilizing flame fusion as disclosed, for example, in U.S. Pat. No. 6,254,981 (Castle), the disclosure of which is incorporated herein by reference. In this method, the metal oxide sources materials are fed (e.g., in the form of particles, sometimes referred to as “feed particles”) directly into a burner (e.g., a methane-air burner, an acetylene-oxygen burner, a hydrogen-oxygen burner, and like), and then quenched, for example, in water, cooling oil, air, or the like. Feed particles can be formed, for example, by grinding, agglomerating (e.g., spray-drying), melting, or sintering the metal oxide sources. The size of feed particles fed into the flame generally determine the size of the resulting amorphous material comprising particles.

Some embodiments of amorphous materials can also be obtained by other techniques, such as: laser spin melt with free fall cooling, Taylor wire technique, plasmatron technique, hammer and anvil technique, centrifugal quenching, air gun splat cooling, single roller and twin roller quenching, roller-plate quenching and pendant drop melt extraction (see, e.g., Rapid Solidification of Ceramics, Brockway et al., Metals And Ceramics Information Center, A Department of Defense Information Analysis Center, Columbus, Ohio, January, 1984, the disclosure of which is incorporated here as a reference). Some embodiments of amorphous materials may also be obtained by other techniques, such as: thermal (including flame or laser or plasma-assisted) pyrolysis of suitable precursors, physical vapor synthesis (PVS) of metal precursors and mechanochemical processing.

Useful amorphous material formulations include those at or near a eutectic composition(s) (e.g., binary and ternary eutectic compositions). In addition to compositions disclosed herein, other compositions, including quaternary and other higher order eutectic compositions, may be apparent to those skilled in the art after reviewing the present disclosure.

Sources, including commercial sources, of (on a theoretical oxide basis) Al₂O₃ include bauxite (including both natural occurring bauxite and synthetically produced bauxite), calcined bauxite, hydrated aluminas (e.g., boehmite, and gibbsite), aluminum, Bayer process alumina, aluminum ore, gamma alumina, alpha alumina, aluminum salts, aluminum nitrates, and combinations thereof. The Al₂O₃ source may contain, or only provide, Al₂O₃. Alternatively, the Al₂O₃ source may contain, or provide Al₂O₃, as well as one or more metal oxides other than Al₂O₃ (including materials of or containing complex Al₂O₃.metal oxides (e.g., Dy₃Al₅O₁₂, Y₃Al₅O₁₂, CeAl₁₁O₁₈, etc.)).

Sources, including commercial sources, of rare earth oxides include rare earth oxide powders, rare earth metals, rare earth-containing ores (e.g., bastnasite and monazite), rare earth salts, rare earth nitrates, and rare earth carbonates. The rare earth oxide(s) source may contain, or only provide, rare earth oxide(s). Alternatively, the rare earth oxide(s) source may contain, or provide rare earth oxide(s), as well as one or more metal oxides other than rare earth oxide(s) (including materials of or containing complex rare earth oxide.other metal oxides (e.g., Dy₃Al₅O₁₂, CeAl₁₁O₁₈, etc.)).

Sources, including commercial sources, of (on a theoretical oxide basis) Y₂O₃ include yttrium oxide powders, yttrium, yttrium-containing ores, and yttrium salts (e.g., yttrium carbonates, nitrates, chlorides, hydroxides, and combinations thereof). The Y₂O₃ source may contain, or only provide, Y₂O₃. Alternatively, the Y₂O₃ source may contain, or provide Y₂O₃, as well as one or more metal oxides other than Y₂O₃ (including materials of or containing complex Y₂O₃.metal oxides (e.g., Y₃Al₅O₁₂)).

Sources, including commercial sources, of (on a theoretical oxide basis) ZrO₂ include zirconium oxide powders, zircon sand, zirconium, zirconium-containing ores, and zirconium salts (e.g., zirconium carbonates, acetates, nitrates, chlorides, hydroxides, and combinations thereof). In addition, or alternatively, the ZrO₂ source may contain, or provide ZrO₂, as well as other metal oxides such as hafnia. Sources, including commercial sources, of (on a theoretical oxide basis) HfO₂ include hafnium oxide powders, hafnium, hafnium-containing ores, and hafnium salts. In addition, or alternatively, the HfO₂ source may contain, or provide HfO₂, as well as other metal oxides such as ZrO₂.

Other useful metal oxide may also include, on a theoretical oxide basis, BaO, CaO, Cr₂O₃, CoO, Fe₂O₃, GeO₂, Li₂O, MgO, MnO, NiO, Na₂O, P₂O₅, Sc₂O₃, SiO₂, SrO, TeO₂, TiO₂, V₂O₃, ZnO, and combinations thereof. Sources, including commercial sources, include the oxides themselves, complex oxides, ores, carbonates, acetates, nitrates, chlorides, hydroxides, etc.

In some embodiments, it may be advantageous for at least a portion of a metal oxide source (in some embodiments, preferably, 10 15, 20, 25, 30, 35, 40, 45,, or even at least 50 percent by weight) to be obtained by adding particulate, metallic material comprising at least one of a metal (e.g., Al, Ca, Cu, Cr, Fe, Li, Mg, Ni, Ag, Ti, Zr, and combinations thereof), M, that has a negative enthalpy of oxide formation or an alloy thereof to the melt, or otherwise metal them with the other raw materials. Although not wanting to be bound by theory, it is believed that the heat resulting from the exothermic reaction associated with the oxidation of the metal is beneficial in the formation of a homogeneous melt and resulting amorphous material. For example, it is believed that the additional heat generated by the oxidation reaction within the raw material eliminates or minimizes insufficient heat transfer, and hence facilitates formation and homogeneity of the melt, particularly when forming amorphous particles with x, y, and z dimensions over 150 micrometers. It is also believed that the availability of the additional heat aids in driving various chemical reactions and physical processes (e.g., densification, and spherodization) to completion. Further, it is believed for some embodiments, the presence of the additional heat generated by the oxidation reaction actually enables the formation of a melt, which otherwise is difficult or otherwise not practical due to high melting point of the materials. Further, the presence of the additional heat generated by the oxidation reaction actually enables the formation of amorphous material that otherwise could not be made, or could not be made in the desired size range. Another advantage of the invention include, in forming the amorphous materials, that many of the chemical and physical processes such as melting, densification and spherodizing can be achieved in a short time, so that very high quench rates be can achieved. For additional details, see copending application having U.S. Ser. No. 10/211,639, filed the same date as the instant application, the disclosure of which is incorporated herein by reference.

The addition of certain metal oxides may alter the properties and/or crystalline structure or microstructure of ceramic comprising abrasive particles according to the present invention, as well as the processing of the raw materials and intermediates in making the ceramic. For example, oxide additions such as MgO, CaO, Li₂O, and Na₂O have been observed to alter both the T_(g) and T_(x) (wherein T_(x) is the crystallization temperature) of glass. Although not wishing to be bound by theory, it is believed that such additions influence glass formation. Further, for example, such oxide additions may decrease the melting temperature of the overall system (i.e., drive the system toward lower melting eutectic), and ease of glass-formation. Complex eutectics in multi component systems (quatemary, etc.) may result in better glass-forming ability. The viscosity of the liquid melt and viscosity of the glass in its “working” range may also be affected by the addition of certain metal oxides such as MgO, CaO, Li₂O, and Na₂O.

Typically, amorphous materials and the glass-ceramics according to the present invention have x, y, and z dimensions each perpendicular to each other, and wherein each of the x, y, and z dimensions is at least 10 micrometers. In some embodiments, the x, y, and z dimensions is at least 30 micrometers, 35 micrometers, 40 micrometers, 45 micrometers, 50 micrometers, 75 micrometers, 100 micrometers, 150 micrometers, 200 micrometers, 250 micrometers, 500 micrometers, 1000 micrometers, 2000 micrometers, 2500 micrometers, 1 mm, or even at least 10 mm. The x, y, and z dimensions of a material are determined either visually or using microscopy, depending on the magnitude of the dimensions. The reported z dimension is, for example, the diameter of a sphere, the thickness of a coating, or the longest length of a prismatic shape.

Crystallization of amorphous material and ceramic comprising the amorphous may also be affected by the additions of certain materials. For example, certain metals, metal oxides (e.g., titanates and zirconates), and fluorides, for example, may act as nucleation agents resulting in beneficial heterogeneous nucleation of crystals. Also, addition of some oxides may change nature of metastable phases devitrifying from the amorphous material upon reheating. In another aspect, for ceramics comprising crystalline ZrO₂, it may be desirable to add metal oxides (e.g., Y₂O₃, TiO₂, CaO, and MgO) that are known to stabilize tetragonal/cubic form of ZrO₂.

The particular selection of metal oxide sources and other additives for making ceramics according to the present invention typically takes into account, for example, the desired composition and microstructure of the resulting crystalline containing ceramics, the desired degree of crystallinity, if any, the desired physical properties (e.g., hardness or toughness) of the resulting ceramics, avoiding or minimizing the presence of undesirable impurities, the desired characteristics of the resulting ceramics, and/or the particular process (including equipment and any purification of the raw materials before and/or during fusion and/or solidification) being used to prepare the ceramics.

In some instances, it may be preferred to incorporate limited amounts of metal oxides selected from the group consisting of: Na₂O, P₂O₅, SiO₂, TeO₂, V₂O₃, and combinations thereof. Sources, including commercial sources, include the oxides themselves, complex oxides, ores, carbonates, acetates, nitrates, chlorides, hydroxides, etc. These metal oxides may be added, for example, to modify a physical property of the resulting abrasive particles and/or improve processing. These metal oxides when used are typically are added from greater than 0 to 20% by weight, preferably greater than 0 to 5% by weight and more preferably greater than 0 to 2% by weight of the glass-ceramic depending, for example, upon the desired property.

The metal oxide sources and other additives can be in any form suitable to the process and equipment being used to make the ceramic comprising abrasive particles according to the present invention. The raw materials can be melted and quenched using techniques and equipment known in the art for making oxide glasses and amorphous metals. Desirable cooling rates include those of 50K/s and greater. Cooling techniques known in the art include roll-chilling. Roll-chilling can be carried out, for example, by melting the metal oxide sources at a temperature typically 20–200° C. higher than the melting point, and cooling/quenching the melt by spraying it under high pressure (e.g., using a gas such as air, argon, nitrogen or the like) onto a high-speed rotary roll(s). Typically, the rolls are made of metal and are water cooled. Metal book molds may also be useful for cooling/quenching the melt.

Other techniques for forming melts, cooling/quenching melts, and/or otherwise forming amorphous materials include vapor phase quenching, plasma spraying, melt-extraction, and gas or centrifugal atomization. Vapor phase quenching can be carried out, for example, by sputtering, wherein the metal alloys or metal oxide sources are formed into a sputtering target(s) which are used. The target is fixed at a predetermined position in a sputtering apparatus, and a substrate(s) to be coated is placed at a position opposing the target(s). Typical pressures of 10⁻³ torr of oxygen gas and Ar gas, discharge is generated between the target(s) and a substrate(s), and Ar or oxygen ions collide against the target to start reaction sputtering, thereby depositing a film of composition on the substrate. For additional details regarding plasma spraying, see, for example, copending application having U.S. Ser. No. 10/211640, filed the same date as the instant application, the disclosure of which is incorporated herein by reference.

Gas atomization involves melting feed particles to convert them to melt. A thin stream of such melt is atomized through contact with a disruptive air jet (i.e., the stream is divided into fine droplets). The resulting substantially discrete, generally ellipsoidal glass particles (e.g., beads) are then recovered. Examples of bead sizes include those having a diameter in a range of about 5 micrometers to about 3 mm. Melt-extraction can be carried out, for example, as disclosed in U.S. Pat. No. 5,605,870 (Strom-Olsen et al.), the disclosure of which is incorporated herein by reference. Containerless glass forming techniques utilizing laser beam heating as disclosed, for example, in PCT application having Publication No. WO 01/27046 A1, published Apr. 4, 2001, the disclosure of which is incorporated herein by reference, may also be useful in making glass according to the present invention.

The cooling rate is believed to affect the properties of the quenched amorphous material. For instance, glass transition temperature, density and other properties of glass typically change with cooling rates.

Rapid cooling may also be conducted under controlled atmospheres, such as a reducing, neutral, or oxidizing environment to maintain and/or influence the desired oxidation states, etc. during cooling. The atmosphere can also influence glass formation by influencing crystallization kinetics from undercooled liquid. For example, larger undercooling of Al₂O₃ melts without crystallization has been reported in argon atmosphere as compared to that in air.

The microstructure or phase composition (glassy/amorphous/crystalline) of a material can be determined in a number of ways. Various information can be obtained using optical microscopy, electron microscopy, differential thermal analysis (DTA), and x-ray diffraction (XRD), for example.

Using optical microscopy, amorphous material is typically predominantly transparent due to the lack of light scattering centers such as crystal boundaries, while crystalline material shows a crystalline structure and is opaque due to light scattering effects.

A percent amorphous yield can be calculated for beads using a −100+120 mesh size fraction (i.e., the fraction collected between 150-micrometer opening size and 125-micrometer opening size screens). The measurements are done in the following manner. A single layer of beads is spread out upon a glass slide. The beads are observed using an optical microscope. Using the crosshairs in the optical microscope eyepiece as a guide, beads that lay along a straight line are counted either amorphous or crystalline depending on their optical clarity. A total of 500 beads are counted and a percent amorphous yield is determined by the amount of amorphous beads divided by total beads counted.

Using DTA, the material is classified as amorphous if the corresponding DTA trace of the material contains an exothermic crystallization event (T_(x)). If the same trace also contains an endothermic event (T_(g)) at a temperature lower than T_(x) it is considered to consist of a glass phase. If the DTA trace of the material contains no such events, it is considered to contain crystalline phases.

Differential thermal analysis (DTA) can be conducted using the following method. DTA runs can be made (using an instrument such as that obtained from Netzsch Instruments, Selb, Germany under the trade designation “NETZSCH STA 409 DTA/TGA”) using a −140+170 mesh size fraction (i.e., the fraction collected between 105-micrometer opening size and 90-micrometer opening size screens). An amount of each screened sample (typically about 400 milligrams (mg)) is placed in a 100-microliter Al₂O₃ sample holder. Each sample is heated in static air at a rate of 10° C./minute from room temperature (about 25° C.) to 1100° C.

Using powder x-ray diffraction, XRD, (using an x-ray diffractometer such as that obtained under the trade designation “PHILLIPS XRG 3100” from Phillips, Mahwah, N.J., with copper K α1 radiation of 1.54050 Angstrom) the phases present in a material can be determined by comparing the peaks present in the XRD trace of the crystallized material to XRD patterns of crystalline phases provided in JCPDS (Joint Committee on Powder Diffraction Standards) databases, published by International Center for Diffraction Data. Furthermore, an XRD can be used qualitatively to determine types of phases. The presence of a broad diffused intensity peak is taken as an indication of the amorphous nature of a material. The existence of both a broad peak and well-defined peaks is taken as an indication of existence of crystalline matter within an amorphous matrix. The initially formed amorphous material or ceramic (including glass prior to crystallization) may be larger in size than that desired. The amorphous material or ceramic can be converted into smaller pieces using crushing and/or comminuting techniques known in the art, including roll crushing, canary milling, jaw crushing, hammer milling, ball milling, jet milling, impact crushing, and the like. In some instances, it is desired to have two or multiple crushing steps. For example, after the ceramic is formed (solidified), it may be in the form of larger than desired. The first crushing step may involve crushing these relatively large masses or “chunks” to form smaller pieces. This crushing of these chunks may be accomplished with a hammer mill, impact crusher or jaw crusher. These smaller pieces may then be subsequently crushed to produce the desired particle size distribution. In order to produce the desired particle size distribution (sometimes referred to as grit size or grade), it may be necessary to perform multiple crushing steps. In general the crushing conditions are optimized to achieve the desired particle shape(s) and particle size distribution. Resulting particles that are of the desired size may be recrushed if they are too large, or “recycled” and used as a raw material for re-melting if they are too small.

The shape of abrasive particles can depend, for example, on the composition and/or microstructure of the ceramic, the geometry in which it was cooled, and the manner in which the ceramic is crushed (i.e., the crushing technique used). In general, where a “blocky” shape is preferred, more energy may be employed to achieve this shape. Conversely, where a “sharp” shape is preferred, less energy may be employed to achieve this shape. The crushing technique may also be changed to achieve different desired shapes. For some particles an average aspect ratio ranging from 1:1 to 5:1 is typically desired, and in some embodiments 1.25:1 to 3:1, or even 1.5:1 to 2.5:1.

It is also within the scope of the present invention, for example, to directly form abrasive particles in desired shapes. For example, abrasive particles may be formed (including molded) by pouring or forming the melt into a mold.

It is also within the scope of the present invention, for example, to fabricate the ceramic (including glass prior to crystallization) by coalescing. This coalescing step in essence forms a larger sized body from two or more smaller particles. For example, amorphous material comprising particles (obtained, for example, by crushing) (including beads and microspheres), fibers, etc. may formed into a larger particle size. For example, ceramic (including glass prior to crystallization), may also be provided by heating, for example, particles comprising the amorphous material, and/or fibers, etc. above the T_(g) such that the particles, etc. coalesce to form a shape and cooling the coalesced shape. The temperature and pressure used for coalescing may depend, for example, upon composition of the amorphous material and the desired density of the resulting material. The temperature should below glass crystallization temperature, and for glasses, greater than the glass transition temperature. In certain embodiments, the heating is conducted at at least one temperature in a range of about 850° C. to about 1100° C. (in some embodiments, preferably 900° C. to 1000° C.). Typically, the amorphous material is under pressure (e.g., greater than zero to 1 GPa or more) during coalescence to aid the coalescence of the amorphous material. In one embodiment, a charge of the particles, etc. is placed into a die and hot-pressing is performed at temperatures above glass transition where viscous flow of glass leads to coalescence into a relatively large part. Examples of typical coalescing techniques include hot pressing, hot isostatic pressure, hot extrusion and the like. Typically, it is generally preferred to cool the resulting coalesced body before further heat treatment. After heat treatment if so desired, the coalesced body may be crushed to smaller particle sizes or a desired particle size distribution.

Glass forms for making abrasive particles according to the present invention, may also be provided by heating, for example, glass or particles comprising glass (including beads, microspheres, and powder (obtained, for example, by crushing) and fibers, etc.) above the T_(g) such that the particles comprising glass, etc. coalesce to form a shape and cooling the coalesced shape. In certain embodiments, the heating is conducted at at least one temperature in a range of about 850° C. to about 1100° C. Typically, the glass is under pressure during coalescence to aid the coalescence of the glass. In one embodiment, a charge of the glass particles, etc. is placed into a die and hot-pressing is performed at temperatures above glass transition where viscous flow of glass leads to coalescence into a relatively large part. It is also within the scope of the present invention to conduct additional heat-treatment to further improve desirable properties of the material. For example, hot-isostatic pressing may be conducted (e.g., at temperatures from about 900° C. to about 1400° C.) to remove residual porosity, increasing the density of the material. It is also within the scope of the present invention to coalesce glass particles, etc. may be conducted via hot-isostatic pressing. Optionally, the resulting, coalesced article can be heat-treated to provide glass-ceramic, crystalline ceramic, or ceramic otherwise comprising crystalline ceramic.

It is also within the scope of the present invention to conduct additional heat-treatment to further improve desirable properties of the material. For example, hot-isostatic pressing may be conducted (e.g., at temperatures from about 900° C. to about 1400° C.) to remove residual porosity, increasing the density of the material. Optionally, the resulting, coalesced article can be heat-treated to provide glass-ceramic, crystalline ceramic, or ceramic otherwise comprising crystalline ceramic.

Coalescing of the amorphous material and/or glass-ceramic (e.g., particles) may also be accomplished by a variety of methods, including pressureless or pressure sintering (e.g., sintering, plasma assisted sintering, hot pressing, IIIPing, hot forging, hot extrusion, etc.).

Heat-treatment can be carried out in any of a variety of ways, including those known in the art for heat-treating glass to provide glass-ceramics. For example, heat-treatment can be conducted in batches, for example, using resistive, inductively or gas heated furnaces. Alternatively, for example, heat-treatment can be conducted continuously, for example, using rotary kilns. In the case of a rotary kiln, the material is fed directly into a kiln operating at the elevated temperature. The time at the elevated temperature may range from a few seconds (in some embodiments even less than 5 seconds) to a few minutes to several hours. The temperature may range anywhere from 900° C. to 1600° C., typically between 1200° C. to 1500° C. It is also within the scope of the present invention to perform some of the heat-treatment in batches (e.g., for the nucleation step) and another continuously (e.g., for the crystal growth step and to achieve the desired density). For the nucleation step, the temperature typically ranges between about 900° C. to about 1100° C., in some embodiments, preferably in a range from about 925° C. to about 1050° C. Likewise for the density step, the temperature typically is in a range from about 1100° C. to about 1600° C., in some embodiments, preferably in a range from about 1200° C. to about 1500° C. This heat treatment may occur, for example, by feeding the material directly into a furnace at the elevated temperature. Alternatively, for example, the material may be feed into a furnace at a much lower temperature (e.g., room temperature) and then heated to desired temperature at a predetermined heating rate. It is within the scope of the present invention to conduct heat-treatment in an atmosphere other than air. In some cases it might be even desirable to heat-treat in a reducing atmosphere(s). Also, for example, it may be desirable to heat-treat under gas pressure as in, for example, hot-isostatic press, or in gas pressure furnace. It is within the scope of the present invention to convert (e.g., crush) the resulting article or heat-treated article to provide particles (e.g., abrasive particles).

The amorphous material is heat-treated to at least partially crystallize the amorphous material to provide glass-ceramic. The heat-treatment of certain glasses to form glass-ceramics is well known in the art. The heating conditions to nucleate and grow glass-ceramics are known for a variety of glasses. Alternatively, one skilled in the art can determine the appropriate conditions from a Time-Temperature-Transformation (TTT) study of the glass using techniques known in the art. One skilled in the art, after reading the disclosure of the present invention should be able to provide TTT curves for glasses according to the present invention, determine the appropriate nucleation and/or crystal growth conditions to provide glass-ceramics according to the present invention.

Typically, glass-ceramics are stronger than the amorphous materials from which they are formed. Hence, the strength of the material may be adjusted, for example, by the degree to which the amorphous material is converted to crystalline ceramic phase(s). Alternatively, or in addition, the strength of the material may also be affected, for example, by the number of nucleation sites created, which may in turn be used to affect the number, and in turn the size of the crystals of the crystalline phase(s). For additional details regarding forming glass-ceramics, see, for example, Glass-Ceramics, P.W. McMillan, Academic Press, Inc., 2^(nd) edition, 1979, the disclosure of which is incorporated herein by reference.

For example, during heat-treatment of some exemplary amorphous materials for making glass-ceramics according to present invention, formation of phases such as La₂Zr₂O₇, and, if ZrO₂ is present, cubic/tetragonal ZrO₂, in some cases monoclinic ZrO₂, have been observed at temperatures above about 900° C. Although not wanting to be bound by theory, it is believed that zirconia-related phases are the first phases to nucleate from the amorphous material. Formation of Al₂O₃, ReAlO₃ (wherein Re is at least one rare earth cation), ReAl₁₁O₁₈, Re₃Al₅O₁₂, Y₃Al₅O₁₂, etc. phases are believed to generaly occur at temperatures above about 925° C. Typically, crystallite size during this nucleation step is on order of nanometers. For example, crystals as small as 10–15 nanometers have been observed. For at least some embodiments, heat-treatment at about 1300° C. for about 1 hour provides a full crystallization. In generally, heat-treatment times for each of the nucleation and crystal growth steps may range of a few seconds (in some embodiments even less than 5 seconds) to several minutes to an hour or more.

Examples of crystalline phases which may be present in ceramics according to the present invention include: complex Al₂O₃.metal oxide(s) (e.g., complex Al₂O₃.REO (e.g., ReAlO₃ (e.g., GdAlO₃ LaAlO₃), ReAl₁₁O₁₈ (e.g., LaAl₁₁O₁₈,), and Re₃Al₅O₁₂ (e.g., Dy₃Al₅O₁₂)), complex Al₂O₃.Y₂O₃ (e.g., Y₃Al₅O₁₂), and complex ZrO₂.REO (e.g., La₂Zr₂O₇)), Al₂O₃ (e.g., α-Al₂O₃), and ZrO₂ (e.g., cubic ZrO₂ and tetragonal ZrO₂).

It is also with in the scope of the present invention to substitute a portion of the yttrium and/or aluminum cations in a complex Al₂O₃.metal oxide (e.g., complex Al₂O₃.Y₂O₃ (e.g., yttrium aluminate exhibiting a garnet crystal structure)) with other cations. For example, a portion of the Al cations in a complex Al₂O₃.Y₂O₃ may be substituted with at least one cation of an element selected from the group consisting of: Cr, Ti, Sc, Fe, Mg, Ca, Si, Co, and combinations thereof. For example, a portion of the Y cations in a complex Al₂O₃.Y₂O₃ may be substituted with at least one cation of an element selected from the group consisting of: Ce, Dy, Er, Eu, Gd, Ho, La, Lu, Nd, Pr, Sm, Th, Tm, Yb, Fe, Ti, Mn, V, Cr, Co, Ni, Cu, Mg, Ca, Sr, and combinations thereof. Similarly, it is also with in the scope of the present invention to substitute a portion of the aluminum cations in alumina. For example, Cr, Ti, Sc, Fe, Mg, Ca, Si, and Co can substitute for aluminum in the alumina. The substitution of cations as described above may affect the properties (e.g. hardness, toughness, strength, thermal conductivity, etc.) of the fused material.

It is also with in the scope of the present invention to substitute a portion of the rare earth and/or aluminum cations in a complex Al₂O₃.metal oxide (e.g., complex Al₂O₃.REO) with other cations. For example, a portion of the Al cations in a complex Al₂O₃.REO may be substituted with at least one cation of an element selected from the group consisting of: Cr, Ti, Sc, Fe, Mg, Ca, Si, Co, and combinations thereof. For example, a portion of the Y cations in a complex Al₂O₃.REO may be substituted with at least one cation of an element selected from the group consisting of: Y, Fe, Ti, Mn, V, Cr, Co, Ni, Cu, Mg, Ca, Sr, and combinations thereof. Similarly, it is also with in the scope of the present invention to substitute a portion of the aluminum cations in alumina. For example, Cr, Ti, Sc, Fe, Mg, Ca, Si, and Co can substitute for aluminum in the alumina. The substitution of cations as described above may affect the properties (e.g. hardness, toughness, strength, thermal conductivity, etc.) of the fused material.

The average crystal size can be determined by the line intercept method according to the ASTM standard E 112-96 “Standard Test Methods for Determining Average Grain Size”. The sample is mounted in mounting resin (such as that obtained under the trade designation “TRANSOPTIC POWDER” from Buehler, Lake Bluff, Ill.) typically in a cylinder of resin about 2.5 cm in diameter and about 1.9 cm high. The mounted section is prepared using conventional polishing techniques using a polisher (such as that obtained from Buehler, Lake Bluff, Ill. under the trade designation “ECOMET 3”). The sample is polished for about 3 minutes with a diamond wheel, followed by 5 minutes of polishing with each of 45, 30, 15, 9, 3, and 1-micrometer slurries. The mounted and polished sample is sputtered with a thin layer of gold-palladium and viewed using a scanning electron microscopy (such as the JEOL SEM Model JSM 840A). A typical back-scattered electron (BSE) micrograph of the microstructure found in the sample is used to determine the average crystal size as follows. The number of crystals that intersect per unit length (N_(L)) of a random straight line drawn across the micrograph are counted. The average crystal size is determined from this number using the following equation.

${{Average}\mspace{14mu}{Crystal}\mspace{14mu}{Size}} = \frac{1.5}{N_{L}M}$

Where N_(L) is the number of crystals intersected per unit length and M is the magnification of the micrograph. Ceramics (including glass-ceramics) comprising abrasive particles according to the present invention comprise at least 1, 2, 3, 5, 10, 15, 20, 25, 30, 35, 40, 45, 50, 55, 60, 65, 70, 75, 80, 85, 90, 95, 97, 98, 99, or even 100 percent by volume crystallites, wherein the crystallites have an average size of less than 1 micrometer. In another aspect, ceramics (including glass-ceramics) comprising abrasive particles according to the present invention comprise less than at least 1, 2, 3, 5, 10, 15, 20, 25, 30, 35, 40, 45, 50, 55, 60, 65, 70, 75, 80, 85, 90, 95, 97, 98, 99, or even 100 percent by volume crystallites, wherein the crystallites have an average size of less than 0.5 micrometer. In another aspect, ceramics (including glass-ceramics) comprising abrasive particles according to the present invention comprise less than at least 1, 2, 3, 5, 10, 15, 20, 25, 30, 35, 40, 45, 50, 55, 60, 65, 70, 75, 80, 85, 90, 95, 97, 98, 99, or even 100 percent by volume crystallites, wherein the crystallites have an average size of less than 0.3 micrometer. In another aspect, ceramics (including glass-ceramics) comprising abrasive particles according to the present invention comprise less than at least 1, 2, 3, 5, 10, 15, 20, 25, 30, 35, 40, 45, 50, 55, 60, 65, 70, 75, 80, 85, 90, 95, 97, 98, 99, or even 100 percent by volume crystallites, wherein the crystallites have an average size of less than 0.15 micrometer.

Crystalline phases that may be present in ceramics according to the present invention may include alumina (e.g., alpha and transition aluminas), REO, HfO₂ ZrO₂, as well as, for example, one or more other metal oxides such as BaO, CaO, Cr₂O₃, CoO, Fe₂O₃, GeO₂, Li₂O, MgO, MnO, NiO, Na₂O, P₂O₅, Sc₂O₃, SiO₂, SrO, TeO₂, TiO₂, V₂O₃, Y₂O₃, ZnO, “complex metal oxides” (including “complex Al₂O₃.metal oxide (e.g., complex Al₂O₃.REO)), and combinations thereof.

Typically, and desirably, the (true) density, sometimes referred to as specific gravity, of ceramic according to the present invention is typically at least 70% of theoretical density. More desirably, the (true) density of ceramic according to the present invention is at least 75%, 80%, 85%, 90%, 95%, 96%, 97%, 98%, 99%, 99.5% or 100% of theoretical density.

Additional details regarding ceramics comprising Al₂O₃, at least one of REO or Y₂O₃, and at least one of ZrO₂ or HfO₂, including making, using, and properties, can be found in application having U.S. Ser. Nos. 09/922,526, 09/922,527, and 09/922,530, filed Aug. 2, 2001, and U.S. Ser. Nos. 10/211,598; 10/211,630; 10/211,639; 10/211,034; 10/211,044; 10/211,628; 10/211,640; 10/211,684, filed the same date as the instant application, the disclosures of which are incorporated herein by reference.

Crystals formed by heat-treating amorphous to provide embodiments of glass-ceramics according to the present invention may be, for example, equiaxed, columnar, or flattened splat-like features.

Although an amorphous material, glass-ceramic, etc. according to the present invention may be in the form of a bulk material, it is also within the scope of the present invention to provide composites comprising an amorphous material, glass-ceramic, etc. according to the present invention. Such a composite may comprise, for example, a phase or fibers (continuous or discontinuous) or particles (including whiskers) (e.g., metal oxide particles, boride particles, carbide particles, nitride particles, diamond particles, metallic particles, glass particles, and combinations thereof) dispersed in an amorphous material, glass-ceramic, etc. according to the present invention, invention or a layered-composite structure (e.g., a gradient of glass-ceramic to amorphous material used to make the glass-ceramic and/or layers of different compositions of glass-ceramics).

Abrasive particles according to the present invention generally comprise crystalline ceramic (e.g., at least 75, 80, 85, 90, 91, 92, 93, 94, 95, 96, 97, 98, 99, 99.5, or even 100 percent by volume) crystalline ceramic. In another aspect, the present invention provides a plurality of particles having a particle size distribution ranging from fine to coarse, wherein at least a portion of the plurality of particles are abrasive particles according to the present invention. In another aspect, embodiments of abrasive particles according to the present invention generally comprise (e.g., at least 75, 80, 85, 90, 91, 92, 93, 94, 95, 96, 97, 98, 99, 99.5, 99.9 or even 100 percent by volume) glass-ceramic.

The average hardness of the material of the present invention can be determined as follows. Sections of the material are mounted in mounting resin (obtained under the trade designation “TRANSOPTIC POWDER” from Buehler, Lake Bluff, Ill.) typically in a cylinder of resin about 2.5 cm in diameter and about 1.9 cm high. The mounted section is prepared using conventional polishing techniques using a polisher (such as that obtained from Buehler, Lake Bluff, Ill. under the trade designation “ECOMET 3”). The sample is polished for about 3 minutes with a diamond wheel, followed by 5 minutes of polishing with each of 45, 30, 15, 9, 3, and 1-micrometer slurries. The microhardness measurements are made using a conventional microhardness tester (such as that obtained under the trade designation “MITUTOYO MVK-VL” from Mitutoyo Corporation, Tokyo, Japan) fitted with a Vickers indenter using a 100-gram indent load. The microhardness measurements are made according to the guidelines stated in ASTM Test Method E384 Test Methods for Microhardness of Materials (1991), the disclosure of which is incorporated herein by reference.

Abrasive particles according to the present invention can be screened and graded using techniques well known in the art, including the use of industry recognized grading standards such as ANSI (American National Standard Institute), FEPA (Federation Europeenne des Fabricants de Products Abrasifs), and JIS (Japanese Industrial Standard). Abrasive particles according to the present invention may be used in a wide range of particle sizes, typically ranging in size from about 0.1 to about 5000 micrometers, more typically from about 1 to about 2000 micrometers; desirably from about 5 to about 1500 micrometers, more desirably from about 100 to about 1500 micrometers.

In a given particle size distribution, there will be a range of particle sizes, from coarse particles fine particles. In the abrasive art this range is sometimes referred to as a “coarse”, “control” and “fine” fractions. Abrasive particles graded according to industry accepted grading standards specify the particle size distribution for each nominal grade within numerical limits. Such industry accepted grading standards include those known as the American National Standards Institute, Inc. (ANSI) standards, Federation of European Producers of Abrasive Products (FEPA) standards, and Japanese Industrial Standard (JIS) standards. ANSI grade designations (i.e., specified nominal grades) include: ANSI 4, ANSI 6, ANSI 8, ANSI 16, ANSI 24, ANSI 36, ANSI 40, ANSI 50, ANSI 60, ANSI 80, ANSI 100, ANSI 120, ANSI 150, ANSI 180, ANSI 220, ANSI 240, ANSI 280, ANSI 320, ANSI 360, ANSI 400, and ANSI 600. Preferred ANSI grades comprising abrasive particles according to the present invention are ANSI 8–220. FEPA grade designations include P8, P12, P16, P24, P36, P40, P50, P60, P80, P100, P120, P150, P180, P220, P320, P400, P500, P600, P800, P1000, and P1200. Preferred FEPA grades comprising abrasive particles according to the present invention are P12–P220. JIS grade designations include JIS8, JIS12, JIS16, JIS24, JIS36, JIS46, JIS54, JIS60, JIS80, JIS100, JIS150, JIS180, JIS220, JIS240, JIS280, JIS320, JIS360, JIS400, JIS600, JIS800, JIS1000, JIS1500, JIS2500, JIS4000, JIS6000, J8000, and JIS10,000. Preferred JIS grades comprising abrasive particles according to the present invention are JIS8–220.

After crushing and screening, there will typically be a multitude of different abrasive particle size distributions or grades. These multitudes of grades may not match a manufacturer's or supplier's needs at that particular time. To minimize inventory, it is possible to recycle the off demand grades back into melt to form glass. This recycling may occur after the crushing step, where the particles are in large chunks or smaller pieces (sometimes referred to as “fines”) that have not been screened to a particular distribution.

In another aspect, the present invention provides a method for making abrasive particles, the method comprising heat-treating glass particles according to the present invention to provide abrasive particles comprising a glass-ceramic according to the present invention. Alternatively, for example, the present invention provides a method for making abrasive particles, the method comprising heat-treating glass according to the present invention, and crushing the resulting heat-treated material to provide abrasive particles comprising a glass-ceramic according to the present invention. When crushed, glass tends to provide sharper particles than crushing significantly crystallized glass-ceramics or crystalline material.

In another aspect, the present invention provides agglomerate abrasive grains each comprised of a plurality of abrasive particles according to the present invention bonded together via a binder. In another aspect, the present invention provides an abrasive article (e.g., coated abrasive articles, bonded abrasive articles (including vitrified, resinoid, and metal bonded grinding wheels, cutoff wheels, mounted points, and honing stones), nonwoven abrasive articles, and abrasive brushes) comprising a binder and a plurality of abrasive particles, wherein at least a portion of the abrasive particles are abrasive particles (including where the abrasive particles are agglomerated) according to the present invention. Methods of making such abrasive articles and using abrasive articles are well known to those skilled in the art. Furthermore, abrasive particles according to the present invention can be used in abrasive applications that utilize abrasive particles, such as slurries of abrading compounds (e.g., polishing compounds), milling media, shot blast media, vibratory mill media, and the like.

Coated abrasive articles generally include a backing, abrasive particles, and at least one binder to hold the abrasive particles onto the backing. The backing can be any suitable material, including cloth, polymeric film, fibre, nonwoven webs, paper, combinations thereof, and treated versions thereof. The binder can be any suitable binder, including an inorganic or organic binder (including thermally curable resins and radiation curable resins). The abrasive particles can be present in one layer or in two layers of the coated abrasive article.

An example of a coated abrasive article is depicted in FIG. 1. Referring to this figure, coated abrasive article 1 has a backing (substrate) 2 and abrasive layer 3. Abrasive layer 3 includes abrasive particles according to the present invention 4 secured to a major surface of backing 2 by make coat 5 and size coat 6. In some instances, a supersize coat (not shown) is used.

Bonded abrasive articles typically include a shaped mass of abrasive particles held together by an organic, metallic, or vitrified binder. Such shaped mass can be, for example, in the form of a wheel, such as a grinding wheel or cutoff wheel. The diameter of grinding wheels typically is about 1 cm to over 1 meter; the diameter of cut off wheels about 1 cm to over 80 cm (more typically 3 cm to about 50 cm). The cut off wheel thickness is typically about 0.5 mm to about 5 cm, more typically about 0.5 mm to about 2 cm. The shaped mass can also be in the form, for example, of a honing stone, segment, mounted point, disc (e.g. double disc grinder) or other conventional bonded abrasive shape. Bonded abrasive articles typically comprise about 3–50% by volume bond material, about 30–90% by volume abrasive particles (or abrasive particle blends), up to 50% by volume additives (including grinding aids), and up to 70% by volume pores, based on the total volume of the bonded abrasive article.

A preferred form is a grinding wheel. Referring to FIG. 2, grinding wheel 10 is depicted, which includes abrasive particles according to the present invention 11, molded in a wheel and mounted on hub 12.

Nonwoven abrasive articles typically include an open porous lofty polymer filament structure having abrasive particles according to the present invention distributed throughout the structure and adherently bonded therein by an organic binder. Examples of filaments include polyester fibers, polyamide fibers, and polyaramid fibers. In FIG. 3, a schematic depiction, enlarged about 100×, of a typical nonwoven abrasive article is provided. Such a nonwoven abrasive article comprises fibrous mat 50 as a substrate, onto which abrasive particles according to the present invention 52 are adhered by binder 54.

Useful abrasive brushes include those having a plurality of bristles unitary with a backing (see, e.g., U.S. Pat. Nos. 5,427,595 (Pihl et al.), 5,443,906 (Pihl et al.), 5,679,067 (Johnson et al.), and 5,903,951 (Ionta et al.), the disclosure of which is incorporated herein by reference). Desirably, such brushes are made by injection molding a mixture of polymer and abrasive particles.

Suitable organic binders for making abrasive articles include thermosetting organic polymers. Examples of suitable thermosetting organic polymers include phenolic resins, urea-formaldehyde resins, melamine-formaldehyde resins, urethane resins, acrylate resins, polyester resins, aminoplast resins having pendant α,β-unsaturated carbonyl groups, epoxy resins, acrylated urethane, acrylated epoxies, and combinations thereof. The binder and/or abrasive article may also include additives such as fibers, lubricants, wetting agents, thixotropic materials, surfactants, pigments, dyes, antistatic agents (e.g., carbon black, vanadium oxide, graphite, etc.), coupling agents (e.g., silanes, titanates, zircoaluminates, etc.), plasticizers, suspending agents, and the like. The amounts of these optional additives are selected to provide the desired properties. The coupling agents can improve adhesion to the abrasive particles and/or filler. The binder chemistry may thermally cured, radiation cured or combinations thereof. Additional details on binder chemistry may be found in U.S. Pat. Nos. 4,588,419 (Caul et al.), 4,751,138 (Tumey et al.), and 5,436,063 (Follett et al.), the disclosures of which are incorporated herein by reference.

More specifically with regard to vitrified bonded abrasives, vitreous bonding materials, which exhibit an amorphous structure and are typically hard, are well known in the art. In some cases, the vitreous bonding material includes crystalline phases. Bonded, vitrified abrasive articles according to the present invention may be in the shape of a wheel (including cut off wheels), honing stone, mounted pointed or other conventional bonded abrasive shape. A preferred vitrified bonded abrasive article according to the present invention is a grinding wheel.

Examples of metal oxides that are used to form vitreous bonding materials include: silica, silicates, alumina, soda, calcia, potassia, titania, iron oxide, zinc oxide, lithium oxide, magnesia, boria, aluminum silicate, borosilicate glass, lithium aluminum silicate, combinations thereof, and the like. Typically, vitreous bonding materials can be formed from composition comprising from 10 to 100% glass frit, although more typically the composition comprises 20% to 80% glass frit, or 30% to 70% glass frit. The remaining portion of the vitreous bonding material can be a non-frit material. Alternatively, the vitreous bond may be derived from a non-frit containing composition. Vitreous bonding materials are typically matured at a temperature(s) in a range of about 700° C. to about 1500° C., usually in a range of about 800° C. to about 1300° C., sometimes in a range of about 900° C. to about 1200° C., or even in a range of about 950° C. to about 1100° C. The actual temperature at which the bond is matured depends, for example, on the particular bond chemistry.

Preferred vitrified bonding materials may include those comprising silica, alumina (desirably, at least 10 percent by weight alumina), and boria (desirably, at least 10 percent by weight boria). In most cases the vitrified bonding material further comprise alkali metal oxide(s) (e.g., Na₂O and K₂O) (in some cases at least 10 percent by weight alkali metal oxide(s)).

Binder materials may also contain filler materials or grinding aids, typically in the form of a particulate material. Typically, the particulate materials are inorganic materials. Examples of useful fillers for this invention include: metal carbonates (e.g., calcium carbonate (e.g., chalk, calcite, marl, travertine, marble and limestone), calcium magnesium carbonate, sodium carbonate, magnesium carbonate), silica (e.g., quartz, glass beads, glass bubbles and glass fibers) silicates (e.g., talc, clays, (montmorillonite) feldspar, mica, calcium silicate, calcium metasilicate, sodium aluminosilicate, sodium silicate) metal sulfates (e.g., calcium sulfate, barium sulfate, sodium sulfate, aluminum sodium sulfate, aluminum sulfate), gypsum, vermiculite, wood flour, aluminum trihydrate, carbon black, metal oxides (e.g., calcium oxide (lime), aluminum oxide, titanium dioxide), and metal sulfites (e.g., calcium sulfite).

In general, the addition of a grinding aid increases the useful life of the abrasive article. A grinding aid is a material that has a significant effect on the chemical and physical processes of abrading, which results in improved performance. Although not wanting to be bound by theory, it is believed that a grinding aid(s) will (a) decrease the friction between the abrasive particles and the workpiece being abraded, (b) prevent the abrasive particles from “capping” (i.e., prevent metal particles from becoming welded to the tops of the abrasive particles), or at least reduce the tendency of abrasive particles to cap, (c) decrease the interface temperature between the abrasive particles and the workpiece, or (d) decreases the grinding forces.

Grinding aids encompass a wide variety of different materials and can be inorganic or organic based. Examples of chemical groups of grinding aids include waxes, organic halide compounds, halide salts and metals and their alloys. The organic halide compounds will typically break down during abrading and release a halogen acid or a gaseous halide compound. Examples of such materials include chlorinated waxes like tetrachloronaphthalene, pentachloronaphthalene, and polyvinyl chloride. Examples of halide salts include sodium chloride, potassium cryolite, sodium cryolite, ammonium cryolite, potassium tetrafluoroborate, sodium tetrafluoroborate, silicon fluorides, potassium chloride, and magnesium chloride. Examples of metals include, tin, lead, bismuth, cobalt, antimony, cadmium, and iron titanium. Other miscellaneous grinding aids include sulfur, organic sulfur compounds, graphite, and metallic sulfides. It is also within the scope of the present invention to use a combination of different grinding aids, and in some instances this may produce a synergistic effect. The preferred grinding aid is cryolite; the most preferred grinding aid is potassium tetrafluoroborate.

Grinding aids can be particularly useful in coated abrasive and bonded abrasive articles. In coated abrasive articles, grinding aid is typically used in the supersize coat, which is applied over the surface of the abrasive particles. Sometimes, however, the grinding aid is added to the size coat. Typically, the amount of grinding aid incorporated into coated abrasive articles are about 50–300 g/m² (desirably, about 80–160 g/m²). In vitrified bonded abrasive articles grinding aid is typically impregnated into the pores of the article.

The abrasive articles can contain 100% abrasive particles according to the present invention, or blends of such abrasive particles with other abrasive particles and/or diluent particles. However, at least about 2% by weight, desirably at least about 5% by weight, and more desirably about 30–100% by weight, of the abrasive particles in the abrasive articles should be abrasive particles according to the present invention. In some instances, the abrasive particles according the present invention may be blended with another abrasive particles and/or diluent particles at a ratio between 5 to 75% by weight, about 25 to 75% by weight about 40 to 60% by weight, or about 50% to 50% by weight (i.e., in equal amounts by weight). Examples of suitable conventional abrasive particles include fused aluminum oxide (including white fused alumina, heat-treated aluminum oxide and brown aluminum oxide), silicon carbide, boron carbide, titanium carbide, diamond, cubic boron nitride, garnet, fused alumina-zirconia, and sol-gel-derived abrasive particles, and the like. The sol-gel-derived abrasive particles may be seeded or non-seeded. Likewise, the sol-gel-derived abrasive particles may be randomly shaped or have a shape associated with them, such as a rod or a triangle. Examples of sol-gel abrasive particles include those described U.S. Pat. Nos. 4,314,827 (Leitheiser et al.), 4,518,397 (Leitheiser et al.), 4,623,364 (Cottringer et al.), 4,744,802 (Schwabel), 4,770,671 (Monroe et al.), 4,881,951 (Wood et al.), 5,011,508 (Wald et al.), 5,090,968 (Pellow), 5,139,978 (Wood), 5,201,916 (Berg et aL), 5,227,104 (Bauer), 5,366,523 (Rowenhorst et al.), 5,429,647 (Larmie), 5,498,269 (Larmie), and 5,551,963 (Larmie), the disclosures of which are incorporated herein by reference. Additional details concerning sintered alumina abrasive particles made by using alumina powders as a raw material source can also be found, for example, in U.S. Pat. Nos. 5,259,147 (Falz), 5,593,467 (Monroe), and 5,665,127 (Moltgen), the disclosures of which are incorporated herein by reference. Additional details concerning fused abrasive particles, can be found, for example, in U.S. Pat. Nos. 1,161,620 (Coulter), 1,192,709 (Tone), 1,247,337 (Saunders et al.), 1,268,533 (Allen), and 2,424,645 (Baumann et al.), 3,891,408 (Rowse et al.), 3,781,172 (Pett et al.), 3,893,826 (Quinan et al.), 4,126,429 (Watson), 4,457,767 (Poon et al.), 5,023,212 (Dubots et al.), 5,143,522 (Gibson et al.), and 5,336,280 (Dubots et al.), and applications having U.S. Ser. Nos. 09/495,978, 09/496,422, 09/496,638, and 09/496,713, each filed on Feb. 2, 2000, and, 09/618,876, 09/618,879, 09/619,106, 09/619,191, 09/619,192, 09/619,215, 09/619,289, 09/619,563, 09/619,729, 09/619,744, and 09/620,262, each filed on Jul. 19, 2000, and 09/772,730, filed Jan. 30, 2001, the disclosures of which are incorporated herein by reference. In some instances, blends of abrasive particles may result in an abrasive article that exhibits improved grinding performance in comparison with abrasive articles comprising 100% of either type of abrasive particle.

If there is a blend of abrasive particles, the abrasive particle types forming the blend may be of the same size. Alternatively, the abrasive particle types may be of different particle sizes. For example, the larger sized abrasive particles may be abrasive particles according to the present invention, with the smaller sized particles being another abrasive particle type. Conversely, for example, the smaller sized abrasive particles may be abrasive particles according to the present invention, with the larger sized particles being another abrasive particle type.

Examples of suitable diluent particles include marble, gypsum, flint, silica, iron oxide, aluminum silicate, glass (including glass bubbles and glass beads), alumina bubbles, alumina beads and diluent agglomerates. Abrasive particles according to the present invention can also be combined in or with abrasive agglomerates. Abrasive agglomerate particles typically comprise a plurality of abrasive particles, a binder, and optional additives. The binder may be organic and/or inorganic. Abrasive agglomerates may be randomly shape or have a predetermined shape associated with them. The shape may be a block, cylinder, pyramid, coin, square, or the like. Abrasive agglomerate particles typically have particle sizes ranging from about 100 to about 5000 micrometers, typically about 250 to about 2500 micrometers. Additional details regarding abrasive agglomerate particles may be found, for example, in U.S. Pat. Nos. 4,311,489 (Kressner), 4,652,275 (Bloecher et al.), 4,799,939 (Bloecher et al.), 5,549,962 (Holmes et al.), and 5,975,988 (Christianson), and applications having U.S. Ser. Nos. 09/688,444 and 09/688,484, filed Oct. 16, 2001, the disclosures of which are incorporated herein by reference.

The abrasive particles may be uniformly distributed in the abrasive article or concentrated in selected areas or portions of the abrasive article. For example, in a coated abrasive, there may be two layers of abrasive particles. The first layer comprises abrasive particles other than abrasive particles according to the present invention, and the second (outermost) layer comprises abrasive particles according to the present invention. Likewise in a bonded abrasive, there may be two distinct sections of the grinding wheel. The outermost section may comprise abrasive particles according to the present invention, whereas the innermost section does not. Alternatively, abrasive particles according to the present invention may be uniformly distributed throughout the bonded abrasive article.

Further details regarding coated abrasive articles can be found, for example, in U.S. Pat. Nos. 4,734,104 (Broberg), 4,737,163 (Larkey), 5,203,884 (Buchanan et al.), 5,152,917 (Pieper et al.), 5,378,251 (Culler et al.), 5,417,726 (Stout et al.), 5,436,063 (Follett et al.), 5,496,386 (Broberg et al.), 5,609,706 (Benedict et al.), 5,520,711 (Helmin), 5,954,844 (Law et al.), 5,961,674 (Gagliardi et al.), and 5,975,988 (Christianson), the disclosures of which are incorporated herein by reference. Further details regarding bonded abrasive articles can be found, for example, in U.S. Pat. Nos. 4,543,107 (Rue), 4,741,743 (Narayanan et al.), 4,800,685 (Haynes et al.), 4,898,597 (Hay et al.), 4,997,461 (Markhoff-Matheny et al.), 5,037,453 (Narayanan et al.), 5,110,332 (Narayanan et al.), and 5,863,308 (Qi et al.) the disclosures of which are incorporated herein by reference. Further details regarding vitreous bonded abrasives can be found, for example, in U.S. Pat. Nos. 4,543,107 (Rue), 4,898,597 (Hay et at.), 4,997,461 (Markhoff-Matheny et at.), 5,094,672

(Giles Jr. et al.), 5,118,326 (Sheldon et at.), 5,131,926 (Sheldon et al.), 5,203,886 (Sheldon et al.), 5,282,875 (Wood et al.), 5,738,696 (Wu et al.), and 5,863,308 (Qi), the disclosures of which are incorporated herein by reference. Further details regarding nonwoven abrasive articles can be found, for example, in U.S. Pat. No. 2,958,593 (Hoover et al.), the disclosure of which is incorporated herein by reference.

The present invention provides a method of abrading a surface, the method comprising contacting at least one abrasive particle according to the present invention, with a surface of a workpiece; and moving at least of one the abrasive particle or the contacted surface to abrade at least a portion of said surface with the abrasive particle. Methods for abrading with abrasive particles according to the present invention range of snagging (i.e., high pressure high stock removal) to polishing (e.g., polishing medical implants with coated abrasive belts), wherein the latter is typically done with finer grades (e.g., less ANSI 220 and finer) of abrasive particles. The abrasive particle may also be used in precision abrading applications, such as grinding cam shafts with vitrified bonded wheels. The size of the abrasive particles used for a particular abrading application will be apparent to those skilled in the art.

Abrading with abrasive particles according to the present invention may be done dry or wet. For wet abrading, the liquid may be introduced supplied in the form of a light mist to complete flood. Examples of commonly used liquids include: water, water-soluble oil, organic lubricant, and emulsions. The liquid may serve to reduce the heat associated with abrading and/or act as a lubricant. The liquid may contain minor amounts of additives such as bactericide, antifoaming agents, and the like.

Abrasive particles according to the present invention may be used to abrade workpieces such as aluminum metal, carbon steels, mild steels, tool steels, stainless steel, hardened steel, titanium, glass, ceramics, wood, wood like materials, paint, painted surfaces, organic coated surfaces and the like. The applied force during abrading typically ranges from about 1 to about 100 kilograms.

Abrasive particles according to the present invention may also be useful, for example, as a filler/reinforcement material in composites (e.g., ceramic, metal, or polymeric (thermosetting or thermoplastic). The particles may, for example, increase the modulus, heat resistance, wear resistance, and/or strength of the matrix material. Although the size, shape, and amount of the particles used to make a composite may depend, for example, on the particular matrix material and use of the composite, the size of the reinforcing particles typically range about 0.1 to 1500 micrometers, more typically 1 to 500 micrometers, and desirably between 2 to 100 micrometers. The amount of particles for polymeric applications is typically about 0.5 percent to about 75 percent by weight, more typically about 1 to about 50 percent by weight. Examples of thermosetting polymers include: phenolic, melamine, urea formaldehyde, acrylate, epoxy, urethane polymers, and the like. Examples of thermoplastic polymers include: nylon, polyethylene, polypropylene, polyurethane, polyester, polyamides, and the like.

Examples of uses for reinforced polymeric materials (i.e., abrasive particles according to the present invention dispersed in a polymer) include protective coatings, for example, for concrete, furniture, floors, roadways, wood, wood-like materials, ceramics, and the like, as well as, anti-skid coatings and injection molded plastic parts and components.

Advantages and embodiments of this invention are further illustrated by the following examples, but the particular materials and amounts thereof recited in these examples, as well as other conditions and details, should not be construed to unduly limit this invention. All parts and percentages are by weight unless otherwise indicated. Unless otherwise stated, all examples contained no significant amount of SiO₂, B₂O₃, P₂O₅, GeO₂, TeO₂, As₂O₃, and V₂O₅.

EXAMPLES Example 1

A polyethylene bottle was charged with 819.6 grams of alumina particles (obtained under the trade designation “APA-0.5” from Condea Vista, Tucson, Ariz.), 818 grams of lanthanum oxide particles (obtained from Molycorp Inc.), 362.4 grams of yttria-stabilized zirconium oxide particles obtained from Zirconia Sales, Inc. of Marietta, Ga. under the trade designation “HSY-3”) and 1050 grams of distilled water. About 2000 grams of the zirconia milling media (obtained from Tosoh Ceramics, Division of Bound Brook, N.J., under the trade designation “YTZ”) were added to the bottle, and the mixture was milled at 120 revolutions per minute (rpm) for 24 hours. After the milling, the milling media were removed and the slurry was poured onto a glass (“PYREX”) pan where it was dried using a heat-gun. The dried mixture was ground with a mortar and pestle and screened through a 70-mesh screen (212-micrometer opening size).

After grinding and screening, some of the particles were fed into a hydrogen/oxygen torch flame. The torch used to melt the particles, thereby generating melted glass beads, was a Bethlehem bench burner PM2D model B, obtained from Bethlehem Apparatus Co., Hellertown, Pa., delivering hydrogen and oxygen at the following rates. For the inner ring, the hydrogen flow rate was 8 standard liters per minute (SLPM) and the oxygen flow rate was 3 SLPM. For the outer ring, the hydrogen flow rate was 23 (SLPM) and the oxygen flow rate was 9.8 SLPM. The dried and sized particles were fed directly into the torch flame, where they were melted and transported to an inclined stainless steel surface (approximately 51 centimeters (cm) (20 inches) wide with the slope angle of 45 degrees) with cold water running over (approximately 8 liters/minute) the surface to form beads.

Examples 2–25

Examples 2–25 beads were prepared as described in Example 1, except the raw materials and the amounts of raw materials, used are listed in Table 1, below, and the milling of the raw materials was carried out in 90 milliliters (ml) of isopropyl alcohol with 200 grams of the zirconia media (obtained from Tosoh Ceramics, Division of Bound Brook, N.J., under the trade designation “YTZ”) at 120 rpm for 24 hours. The sources of the raw materials used are listed in Table 2, below.

TABLE 1 Example Weight percent of components Batch amounts, g  2* La₂O₃: 48 La₂O₃ 240 Al₂O₃: 52 Al₂O₃: 260  3 La₂O₃: 43 La₂O₃:  21.5 Al₂O₃: 32 Al₂O₃:  16 ZrO₂: 12 ZrO₂:  6 SiO₂: 13 SiO₂:  6.5  4 La₂O₃: 45.06 La₂O₃:  22.53 Al₂O₃: 34.98 Al₂O₃:  17.49 ZrO₂: 19.96 ZrO₂:  9.98  5 La₂O₃: 38.65 La₂O₃:  19.33 Al₂O₃: 38.73 Al₂O₃:  19.37 ZrO₂: 22.62 ZrO₂:  11.31  6 La₂O₃: 32.58 La₂O₃:  16.2 Al₂O₃: 52.98 Al₂O₃:  26.49 ZrO₂: 14.44 ZrO₂:  7.22  7 CeO₂: 41.4 CeO₂:  20.7 Al₂O₃: 40.6 Al₂O₃:  20.3 ZrO₂: 18 ZrO₂:  9.00  8 Al₂O₃: 41.0 Al₂O₃:  20.5 ZrO₂: 18.0 ZrO₂:  9.0 Gd₂O₃: 41.0 Gd₂O₃:  20.5  9 Al₂O₃: 40.9 Al₂O₃:  20.45 Er₂O₃: 40.9 Er₂O₃:  20.45 ZrO₂: 18.2 ZrO₂:  9.1 10 La₂O₃: 35.0 La₂O₃:  17.5 Al₂O₃: 40.98 Al₂O₃:  20.49 ZrO₂: 18.12 ZrO₂:  9.06 Nd₂O₃:  5.0 Nd₂O₃:  2.50 11 La₂O₃: 35.0 La₂O₃:  17.5 Al₂O₃: 40.98 Al₂O₃:  20.49 ZrO₂: 18.12 ZrO₂:  9.06 CeO₂:  5.0 CeO₂:  2.50 12 HfO₂: 35.5 HfO₂:  17.75 Al₂O₃: 32.5 Al₂O₃:  16.25 La₂O₃: 32.5 La₂O₃:  16.25 13 La₂O₃: 41.7 La₂O₃:  20.85 Al₂O₃: 35.4 Al₂O₃:  17.7 ZrO₂: 16.9 ZrO₂:  8.45 MgO:  6.0 MgO:  3.0 14 La₂O₃: 43.02 La₂O₃:  21.51 Al₂O₃: 36.5 Al₂O₃:  18.25 ZrO₂: 17.46 ZrO₂:  8.73 Li₂CO₃:  3.0 Li₂CO₃:  1.50 15 La₂O₃: 38.8 La₂O₃:  19.4 Al₂O₃: 40.7 Al₂O₃:  20.35 ZrO₂: 17.5 ZrO₂:  8.75 Li₂CO₃:  6 Li₂CO₃  3 16 La₂O₃: 43.02 La₂O₃:  21.51 Al₂O₃: 36.5 Al₂O₃:  18.25 ZrO₂: 17.46 ZrO₂:  8.73 TiO₂: 3% TiO₂:  1.50 17 Y₂O₃: 45.06 Y₂O₃:  14.35 Al₂O₃: 34.98 Al₂O₃:  26.35 ZrO₂: 19.96 ZrO₂:  9.3 18 Y₂O₃: 27.6 Y₂O₃:  13.8 Al₂O₃: 57.5 Al₂O₃:  23.75 ZrO₂: 14.9 ZrO₂:  7.45 19 Y₂O₃: 27.44 Y₂O₃:  13.72 Al₂O₃: 57.14 Al₂O₃:  28.57 ZrO₂: 15.43 ZrO₂:  7.71 20 Y₂O₃: 28.7 Y₂O₃:  14.35 Al₂O₃: 55.7 Al₂O₃:  27.85 ZrO₂: 15.5 ZrO₂:  7.75 21 Y₂O₃: 19 Y₂O₃:  9.5 Al₂O₃: 51 Al₂O₃:  25.5 ZrO₂: 17.9 ZrO₂:  8.95 La₂O₃: 12.1 La₂O₃:  6.05 22 Y₂O₃: 19.3 Y₂O₃:  9.65 Al₂O₃: 50.5 Al₂O₃:  25.25 ZrO₂: 17.8 ZrO₂:  8.9 Nd₂O₃: 12.4 Nd₂O₃:  6.2 23 Y₂O₃: 27.4 Y₂O₃:  13.7 Al₂O₃: 50.3 Al₂O₃:  25.15 ZrO₂: 17.8 ZrO₂:  8.9 Li₂CO₃:  4.5 Li₂CO₃:  2.25 24 HfO₂: 20.08 HfO₂:  14.04 Al₂O₃: 46.55 Al₂O₃:  23.27 Y₂O₃: 25.37 Y₂O₃:  12.67 25 Y₂O₃: 27.4 Y₂O₃:  13.7 Al₂O₃: 50.3 Al₂O₃:  25.15 ZrO₂: 17.8 ZrO₂:  8.9 MgO:  4.5 MgO:  2.25 *For this example, same milling procedure as in Example 1 was used.

TABLE 2 Raw Material Source Alumina particles Obtained from Condea Vista, (Al₂O₃) Tucson, AZ under the trade designation “APA-0.5” Calcium oxide particles Obtained from Alfa Aesar, (CaO) Ward Hill, MA Cerium oxide particles Obtained from Rhone-Poulenc, (CeO₂) France Erbium oxide particles Obtained from Aldrich (Er₂O₃) Chemical Co., Milwaukee, WI Gadolinium oxide Obtained from Molycorp Inc., particles (Gd₂O₃) Mountain Pass, CA Hafnium oxide particles Obtained from Teledyne Wah (HfO₂) Chang Albany Company, Albany, OR Lanthanum oxide Obtained from Molycorp Inc., particles (La₂O₃) Mountain Pass, CA Lithium carbonate Obtained from Aldrich particles (Li₂CO₃) Chemical Co. Magnesium oxide Obtained from Aldrich particles (MgO) Chemical Co. Neodymium oxid Obtained from Molycorp Inc. particles (Nd₂O₃) Silica particles (SiO₂) Obtained from Alfa Aesar, Ward Hill, MA Sodium bicarbonate Obtained from Aldrich particles (NaHCO₃) Chemical Co. Titanium dioxide Obtained from Kemira Inc., particles (TiO₂) Savannah, GA Yttria-stabilized Obtained from Zirconia Sales, zirconium oxide Inc. of Marietta, GA under particles (Y-PSZ) the trade designation “HSY-3” Yttrium oxide particles Obtained from H. C. Stark (Y₂O₃) Newton, MA

Various properties/characteristics of some Example 1–25 material were measured as foltows. Powder X-ray diffraction (using an X-ray diffractometer (obtained under the trade designation “PHILLIPS XRG 3100” from PHILLIPS, Mahwah, N.J.) with copper K<1 radiation of 1.54050 Angstrom) was used to qualitatively measure phases present in example materials. The presence of a broad diffused intensity peak was taken as an indication of the amorphous nature of a material. The existence of both a broad peak and well-defined peaks was taken as an indication of the existence of crystalline matter within an amorphous matrix. Phases detected in various examples are reported in Table 3, below.

TABLE 3 Phases detected Hot- via X-ray pressing Example diffraction Color T_(g),° C. T_(x), ° C. temp, ° C. 1 Amorphous* Clear 834 937 960 2 Amorphous* Clear 840 925 960 3 Amorphous* Clear 837 1001 — 4 Amorphous* Clear 837 936 — 5 Amorphous* Clear 850 923 — 6 Amorphous* Clear/ 858 914 965 and milky Crystalline 7 Amorphous* Brown 838 908 960 and Crystalline 8 Amorphous* Clear 886 933 985 9 Amorphous* Intense pink 858 914 — 10 Amorphous* Blue/ 836 930 965 purple 11 Amorphous* Yellow 831 934 965 12 Amorphous* Clear/ 828 937 960 greenish 13 Amorphous* Clear 795 901 950 14 Amorphous* Clear 816 942 950 15 Amorphous* Clear 808 940 950 16 Amorphous* Clear/ 834 935 950 Greenish 17 Amorphous* Clear/ 865 941 980 and milky Crystalline 18 Amorphous* Clear/ 871 934 — and milky Crystalline 19 Amorphous* Clear/ 874 937 — and milky Crystalline 20 Amorphous* Clear/ 870 942 — and milky Crystalline 21 Amorphous* Clear 843 938 970 22 Amorphous* Blue/ 848 934 970 pink 23 Amorphous* Clear 852 941 970 24 Amorphous* Clear/ 867 948 — and Greenish Crystalline 25 Amorphous* Clear/ 869 934 — and milky Crystalline *glass, as the example has a T_(g)

For differential thermal analysis (DTA), a material was screened to retain beads in the 90–125 micrometer size range. DTA runs were made (using an instrument obtained from Netzsch Instruments, Selb, Germany under the trade designation “NETZSCH STA 409 DTA/TGA”). The amount of each screened sample placed in a 100-microliter Al₂O₃ sample holder was 400 milligrams. Each sample was heated in static air at a rate of 10° C./minute from room temperature (about 25° C.) to 1200° C.

Referring to FIG. 4, line 123 is the plotted DTA data for the Example 1 material. Referring to FIG. 4 line 123, the material exhibited an endothermic event at a temperature around 834° C., as evidenced by the downward curve of line 123. It was believed that this event was due to the glass transition (T_(g)) of the glass material. At about 937° C., an exothermic event was observed as evidenced by the sharp peak in line 123. It was believed that this event was due to the crystallization (T_(x)) of the material. These T_(g) and T_(x) values for other examples are reported in Table 3, above.

For each of Examples 1–25, about 25 grams of the beads were placed in a graphite die and hot-pressed using uniaxial pressing apparatus (obtained under the trade designation “HP-50”, Thermal Technology Inc., Brea, Calif.). The hot-pressing was carried out in an argon atmosphere and 13.8 megapascals (MPa) (2000 pounds per square inch (2 ksi)) pressure. The hot-pressing temperature at which appreciable glass flow occurred, as indicated by the displacement control unit of the hot pressing equipment described above, is reported for various examples in Table 3, above. About 400 grams of Example 1 beads and 200 grams of Example 2 beads were hot-pressed.

Example 1–25 beads were heat-treated in a furnace (an electrically heated furnace (obtained under the trade designation “Model KKSK-666-3100” from Keith Furnaces of Pico Rivera, Calif.)) as follows. The beads were heated from room temperature (about 25° C.) to about 1300° C. at a rate of about 10° C./minute and then held at 1300° C. for about 1 hour before cooling back to room temperature by turning off the furnace.

FIGS. 5–9 are scanning electron microscope (SEM) photomicrographs of a polished section of heat-treated Examples 2, 6, 7, 8, and 17 materials, respectively. The polished sections were prepared using conventional mounting and polishing techniques. Polishing was done using a polisher (obtained from Buehler of Lake Bluff, Ill. under the trade designation “ECOMET 3 TYPE POLISHER-GRINDER”). The sample was polished for about 3 minutes with a diamond wheel, followed by three minutes of polishing with each of 45, 30, 15, 9, and 3-micrometer diamond slurries. The polished sample was sputter coated with a thin layer of gold-palladium and viewed using JEOL SEM (Model JSM 840A).

Phases present after heat-treatment were analyzed using powder X-ray diffraction techniques as described above. The results are summarized in Table 4, below.

TABLE 4 Phases detected via X-ray Example diffraction Hardness, GPa 1 Cubic/tetragonal ZrO₂ 16.4 ± 0.3 α-Al₂O₃ LaAl₁₁O₁₈ LaAlO₃ 2 LaAl₁₁O₁₈ 16.0 ± 0.4 LaAlO₃ 6 Cubic/tetragonal ZrO₂ 16.7 ± 0.2 α-Al₂O₃ LaAl₁₁O₁₈ LaAlO₃ 8 Cubic/tetragonal ZrO₂ 16.9 ± 0.1 GdAlO₃ α-Al₂O₃ 17 Cubic/tetragonal ZrO₂ 17.4 ± 0.4 Y₃Al₅O₁₂ α-Al₂O₃ 21 Cubic/tetragonal ZrO₂ Y₃Al₅O₁₂ LaAlO₃ α-Al₂O₃ 23 Cubic/tetragonal ZrO₂ 16.9 ± 0.3 Y₃Al₅O₁₂ α-Al₂O₃

The average microhardnesses of heat-treated beads from selected Examples were measured by mounting loose beads (about 125 micrometers in size) in mounting resin (obtained under the trade designation “ECOMET 3” from Buehler Ltd., Lake Bluff, Ill.). The resulting cylinder of resin was about 2.5 cm (1 inch) in diameter and about 1.9 cm (0.75 inch) high. The mounted samples were polished using a conventional grinder/polisher (obtained under the trade designation “ECOMET 3” from Buehler Ltd.) and conventional diamond slurries with the final polishing step using a 1-micrometer diamond slurry (obtained under the trade designation “METADI” from Buehler Ltd.) to obtain polished cross-sections of the sample.

The microhardness measurements were made using a conventional microhardness tester (obtained under the trade designation “MITUTOYO MVK-VL” from Mitutoyo Corporation, Tokyo, Japan) fitted with a Vickers indenter using a 500-gram indent load. The microhardness measurements were made according to the guidelines stated in ASTM Test Method E384 Test Methods for Microhardness of Materials (1991), the disclosure of which is incorporated herein by reference. The microhardness values were an average of 20 measurements. The average microhardness values are reported in Table 4, above.

Grinding Performance of Examples 1, 1A, and 2 and Comparative Examples A–C

Examples 1 and 2 hot-pressed material was crushed by using a “Chipmunk” jaw crusher (Type VD, manufactured by BICO Inc., Burbank, Calif.) into (abrasive) particles and graded to retain the −25+30 mesh fraction (i.e., the fraction collected between 25-micrometer opening size and 30-micrometer opening size sieves) and −30+35 mesh fractions (i.e., the fraction collected between 30-micrometer opening size and 35-micrometer opening size sieves) (USA Standard Testing Sieves). These two mesh fractions were combined to provide a 50/50 blend. The blended material was heat treated at 1300° C. for 1 hour as described above. Thirty grams of the resulting glass-ceramic abrasive particles were incorporated into a coated abrasive disc. The coated abrasive disc was made according to conventional procedures. The glass-ceramic abrasive particles were bonded to 17.8 cm diameter, 0.8 mm thick vulcanized fiber backings (having a 2.2 cm diameter center hole) using a conventional calcium carbonate-filled phenolic make resin (48% resole phenolic resin, 52% calcium carbonate, diluted to 81% solids with water and glycol ether) and a conventional cryolite-filled phenolic size resin (32% resole phenolic resin, 2% iron oxide, 66% cryolite, diluted to 78% solids with water and glycol ether). The wet make resin weight was about 185 g/m². Immediately after the make coat was applied, the glass-ceramic abrasive particles were electrostatically coated. The make resin was precured for 120 minutes at 88° C. Then the cryolite-filled phenolic size coat was coated over the make coat and abrasive particles. The wet size weight was about 850 grams per square (g/m²). The size resin was cured for 12 hours at 99° C. The coated abrasive discs were flexed prior to testing.

Example 1A coated abrasive disk was prepared as described for Example 1 except the Example 1A abrasive particles were obtained by crushing a hot-pressed and heat-treated Example 1 material, rather than crushing then heat-treating.

Comparative Example A coated abrasive discs were prepared as described for Example 6 (above), except heat-treated fused alumina abrasive particles (obtained under the trade designation “ALODUR BFRPL” from Triebacher, Villach, Austria) was used in place of the Example 1 glass-ceramic abrasive particles.

Comparative Example B coated abrasive discs were prepared as described for Example 6 (above), except alumina-zirconia abrasive particles (having a eutectic composition of 53% Al₂O₃ and 47% ZrO₂; obtained under the trade designation “NORZON” from Norton Company, Worcester, Mass.) were used in place of the Example 1 glass-ceramic abrasive particles.

Comparative Example C coated abrasive discs were prepared as described above except sol-gel-derived abrasive particles (marketed under the trade designation “321 CUBITRON” from the 3M Company, St. Paul, Minn.) were used in place of the Example 1 glass-ceramic abrasive particles.

The grinding performance of Examples 1, 1A, 2, and Comparative Examples A-C coated abrasive discs were evaluated as follows. Each coated abrasive disc was mounted on a beveled aluminum back-up pad, and used to grind the face of a pre-weighed 1.25 cm×18 cm×10 cm 1018 mild steel workpiece. The disc was driven at 5,000 rpm while the portion of the disc overlaying the beveled edge of the back-up pad contacted the workpiece at a load of 8.6 kilograms. Each disc was used to grind an individual workpiece in sequence for one-minute intervals. The total cut was the sum of the amount of material removed from the workpieces throughout the test period. The total cut by each sample after 12 minutes of grinding as well as the cut at the 12th minute (i.e., the final cut) are reported in Table 6, below. The Example 1 results are an average of two discs, where as one disk was tested for each of Example 1A and Comparative Examples A, B, and C.

TABLE 6 Example Total cut, g Final cut, g 1 1163 91 1 A 1197 92 2 1094 91 Comp. A 514 28 Comp. B 689 53 Comp. C 1067 89

Various modifications and alterations of this invention will become apparent to those skilled in the art without departing from the scope and spirit of this invention, and it should be understood that this invention is not to be unduly limited to the illustrative embodiments set forth herein. 

1. Abrasive particle comprising a glass-ceramic comprising Al₂O₃ and REO, wherein at least 80 percent by weight of the glass-ceramic collectively comprises the Al₂O₃ and REO, based on the total weight of the glass-ceramic.
 2. The abrasive particle according to claim 1 comprising at least 90 percent by volume of said glass-ceramic, based on the total volume of said abrasive particle.
 3. Abrasive particle comprising a glass-ceramic comprising Al₂O₃ and REO, wherein at least 60 percent by weight of the glass-ceramic collectively comprises the Al₂O₃ and REO, and less than 20 percent by weight SiO₂ and less than 20 percent by weight B₂O₃, based on the total weight of the glass-ceramic.
 4. The abrasive particle according to claim 3 comprising at least 90 percent by volume of said glass-ceramic, based on the total volume of said abrasive particle.
 5. Abrasive particle comprising a glass-ceramic comprising Al₂O₃ and REO, wherein at least 60 percent by weight of the glass-ceramic collectively comprises the Al₂O₃ and REO, and less than 40 percent by weight collectively SiO₂, B₂O₃, and P₂O₅, based on the total weight of the glass-ceramic.
 6. The abrasive particle according to claim 5 comprising at least 90 percent by volume of said glass-ceramic, based on the total volume of said abrasive particle.
 7. Abrasive particle comprising a glass-ceramic comprising Al₂O₃ and REO, wherein the ceramic (a) exhibits a microstructure comprising crystallites having an average crystallite size of less than 1 micrometer, and (b) is free of eutectic microstructure features.
 8. The abrasive particle according to claim 7 comprising at least 90 percent by volume of said glass-ceramic, based on the total volume of said abrasive particle.
 9. A method for making abrasive particles, the method comprising: heat-treating glass particles comprising Al₂O₃ and REO, wherein at least 80 percent by weight of the glass collectively comprises the Al₂O₃ and REO, based on the total weight of the glass particles, to provide glass-ceramic abrasive particles.
 10. A method for making abrasive particles, the method comprising: heat-treating particles comprising glass, wherein the glass comprises Al₂O₃ and REO, wherein at least 80 percent by weight of the glass collectively comprises the Al₂O₃ and REO, based on the total weight of the glass particles, to provide glass-ceramic abrasive particles.
 11. A method for making abrasive particles, the method comprising: heat-treating glass comprising Al₂O₃ and REO, wherein at least 80 percent by weight of the glass collectively comprises the Al₂O₃ and REO, based on the total weight of the glass, to provide glass-ceramic; and converting the glass-ceramic to provide abrasive particles.
 12. A method for making abrasive particles, the method comprising: heat-treating ceramic comprising glass, wherein the glass comprises Al₂O₃ and REO, wherein at least 80 percent by weight of the glass collectively comprises the Al₂O₃ and REO, based on the total weight of the glass, to provide glass-ceramic; and converting the glass-ceramic to provide abrasive particles.
 13. A method for making abrasive particles, the method comprising: heat-treating glass particles comprising Al₂O₃ and REO, wherein at least 60 percent by weight of the glass collectively comprises the Al₂O₃ and REO, and less than 20 percent by weight SiO₂ and less than 20 percent by weight B₂O₃, based on the total weight of the glass particles, to provide glass-ceramic abrasive particles.
 14. A method for making abrasive particles, the method comprising: heat-treating particles comprising glass, wherein the glass comprises Al₂O₃ and REO, wherein at least 60 percent by weight of the glass collectively comprises the Al₂O₃ and REO, and less than 20 percent by weight SiO₂ and less than 20 percent by weight B₂O₃, based on the total weight of the glass particles, to provide glass-ceramic abrasive particles.
 15. A method for making abrasive particles, the method comprising: heat-treating glass comprising Al₂O₃ and REO, wherein at least 60 percent by weight of the glass collectively comprises the Al₂O₃ and REO, and less than 20 percent by weight SiO₂ and less than 20 percent by weight B₂O₃, based on the total weight of the glass, to provide glass-ceramic; and converting the glass-ceramic to provide abrasive particles.
 16. A method for making abrasive particles, the method comprising: heat-treating ceramic comprising glass, wherein the glass comprises Al₂O₃ and REO, wherein at least 60 percent by weight of the glass collectively comprises the Al₂O₃ and REO, and less than 20 percent by weight SiO₂ and less than 20 percent by weight B₂O₃, based on the total weight of the glass, to provide glass-ceramic; and converting the glass-ceramic to provide abrasive particles.
 17. A method for making abrasive particles, the method comprising: heat-treating glass particles comprising Al₂O₃ and REO, wherein at least 60 percent by weight of the glass collectively comprises the Al₂O₃ and REO, and less than 40 percent by weight collectively SiO₂, B₂O₃, and P₂O₅, based on the total weight of the glass particles, to provide glass-ceramic abrasive particles.
 18. A method for making abrasive particles, the method comprising: heat-treating particles comprising glass, wherein the glass comprises Al₂O₃ and REO, wherein at least 60 percent by weight of the glass collectively comprises the Al₂O₃ and REO, and less than 40 percent by weight collectively SiO₂, B₂O₃, and P₂O₅, based on the total weight of the glass particles, to provide glass-ceramic abrasive particles.
 19. A method for making abrasive particles, the method comprising: heat-treating glass comprising Al₂O₃ and REO, wherein at least 60 percent by weight of the glass collectively comprises the Al₂O₃ and REO, and less than 40 percent by weight collectively SiO₂, B₂O₃, and P₂O₅, based on the total weight of the glass, to provide glass-ceramic; and converting the glass-ceramic to provide abrasive particles.
 20. A method for making abrasive particles, the method comprising: heat-treating ceramic comprising glass, wherein the glass comprises Al₂O₃ and REO, wherein at least 60 percent by weight of the glass collectively comprises the Al₂O₃ and REO, and less than 40 percent by weight collectively SiO₂, B₂O₃, and P₂O₅, based on the total weight of the glass, to provide glass-ceramic; and converting the glass-ceramic to provide abrasive particles.
 21. A method for making abrasive particles, the method comprising: heat-treating glass particles comprising Al₂O₃ and REO to provide glass-ceramic abrasive particles, wherein the glass-ceramic (a) exhibits a microstructure comprising crystallites having an average crystallite size of less than 1 micrometer, and (b) is free of eutectic microstructure features.
 22. A method for making abrasive particles, the method comprising: heat-treating particles comprising glass, wherein the glass comprises Al₂O₃ and REO to provide glass-ceramic abrasive particles, wherein the glass-ceramic (a) exhibits a microstructure comprising crystallites having an average crystallite size of less than 1 micrometer, and (b) is free of eutectic microstructure features.
 23. A method for making abrasive particles, the method comprising: heat-treating glass comprising Al₂O₃ and REO to provide glass-ceramic, wherein the glass-ceramic (a) exhibits a microstructure comprising crystallites having an average crystallite size of less than 1 micrometer, and (b) is free of eutectic microstructure features; and converting the glass-ceramic to provide abrasive particles.
 24. A method for making abrasive particles, the method comprising: heat-treating ceramic comprising glass, wherein the glass comprises Al₂O₃ and REO to provide glass-ceramic, wherein the glass-ceramic (a) exhibits a microstructure comprising crystallites having an average crystallite size of less than 1 micrometer, and (b) is free of eutectic microstructure features; and converting the glass-ceramic to provide abrasive particles.
 25. Abrasive particle comprising a glass-ceramic comprising Al₂O₃ and REO, wherein the glass-ceramic (a) exhibits a microstructure comprising crystallites having an average crystallite size of less than 200 nanometers and (b) has a density of at least 90% of theoretical density.
 26. The abrasive particle according to claim 25 comprising at least 90 percent by volume of said ceramic, based on the total volume of said abrasive particle.
 27. Abrasive particle comprising a glass-ceramic comprising Al₂O₃ and REO, wherein the glass-ceramic (a) exhibits a microstructure comprising crystallites, wherein none of the crystallites are greater than 200 nanometers in size and (b) has a density of at least 90% of theoretical density.
 28. The abrasive particle according to claim 27 comprising at least 90 percent by volume of said ceramic, based on the total volume of said abrasive particle.
 29. Abrasive particle comprising a glass-ceramic comprising Al₂O₃ and REO, wherein the glass-ceramic (a) exhibits a microstructure comprising crystallites, wherein at least a portion of the crystallites are not greater than 150 nanometers in size and (b) has a density of at least 90% of theoretical density.
 30. The abrasive particle according to claim 29 comprising at least 90 percent by volume of said ceramic, based on the total volume of said abrasive particle.
 31. Abrasive particle comprising ceramic comprising at least 75 percent by volume glass-ceramic, the glass-ceramic comprising Al₂O₃ and REO, wherein the ceramic (a) exhibits a microstructure comprising crystallites having an average crystallite size of less than 200 nanometers and (b) has a density of at least 90% of theoretical density.
 32. The abrasive particle according to claim 31 comprising at least 90 percent by volume of said ceramic, based on the total volume of said abrasive particle.
 33. Abrasive particle comprising ceramic comprising at least 75 percent by volume glass-ceramic, the glass-ceramic comprising Al₂O₃ and REO, wherein the ceramic (a) exhibits a microstructure comprising crystallites, wherein none of the crystallites are greater than 200 nanometers in size and (b) has a density of at least 90% of theoretical density.
 34. The abrasive particle according to claim 33 comprising at least 90 percent by volume of said ceramic, based on the total volume of said abrasive particle.
 35. Abrasive particle comprising ceramic comprising at least 75 percent by volume glass-ceramic, the glass-ceramic comprising Al₂O₃ and REO, wherein the ceramic (a) exhibits a microstructure comprising crystallites, wherein at least a portion of the crystallites are not greater than 150 nanometers in size and (b) has a density of at least 90% of theoretical density.
 36. The abrasive particle according to claim 35 comprising at least 90 percent by volume of said ceramic, based on the total volume of said abrasive particle.
 37. Abrasive particle comprising ceramic comprising at least 75 percent by volume glass-ceramic, the glass-ceramic comprising Al₂O₃ and REO, wherein the ceramic (a) exhibits a microstructure comprising crystallites having an average crystallite size not greater than 200 nanometer, in size and (b) has a density of at least 90% of theoretical density.
 38. The abrasive particle according to claim 37 comprising at least 90 percent by volume of said ceramic, based on the total volume of said abrasive particle. 